牌号简介 About |
---|
说明:EPOCAST1628-A环氧树脂是一种白色软浆,与黄色EPOCAST1628-B硬化剂混合后,变成淡黄色、超低密度的环氧树脂复合材料,用于蜂窝结构的边缘加固。轻量的环氧树脂糊可以用油灰刀或泥刀涂满蜂窝芯段或复合夹层结构的边缘。EPOCAST1628-A/B环氧树脂固化后,可轻易打磨或机加工。EPOCAST 1628-A/B环氧树脂句法符合BMS 5-28,类型28。 DESCRIPTION: Epocast® 1628-A epoxy resin is a soft white paste that, after blending with yellow-colored Epocast® 1628-B hardener, becomes a pale yellow, ultra low density epoxy syntactic for edge reinforcing of honeycomb structures. The lightweight epoxy paste can be spread with a putty knife or trowel to fill honeycomb core sections or edges of composite sandwich constructions. Epocast® 1628-A/B epoxy syntactic can be easily sanded or machined after cure. Epocast® 1628-A/B epoxy syntactic is qualified to BMS 5-28, Type 28. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
ASTM D1622 | ||
-- -- 2 |
0.450 | g/cm³ | ASTM D1622 |
-- -- 3 |
0.500 | g/cm³ | ASTM D1622 |
-- -- 4 |
0.520 | g/cm³ | ASTM D1622 |
粘度 viscosity |
ASTM D2196 | ||
-- -- 2 |
Paste | ASTM D2196 | |
-- -- 3 |
Paste | ASTM D2196 | |
-- -- 4 |
ASTM D2196 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
|||
25℃ 25℃ |
MPa | ASTM D695 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 5 |
FAR 25.853 | ||
烧伤长度 Burn length |
cm | ||
熄灭时间 Extinguishing time |
hr | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
胶凝时间 Gelation time |
|||
60 gms,25℃ 60 gms,25℃ |
hr | ASTM D2471 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
25℃ 25℃ |
day | ||
Tensile Lap Shear(etched al/al,25℃) Tensile Lap Shear(etched al/al,25℃) |
MPa | ASTM D1002 | |
体重增量 Weight gain 6 |
ASTM D543 | ||
Distilled water:25℃ Distilled water:25℃ |
% | ASTM D543 | |
Mil-M-5606,hydraulic fluid:25℃ Mil-M-5606,hydraulic fluid:25℃ |
% | ASTM D543 | |
Mil-S-3136,Type III test fluid:25℃ Mil-S-3136,Type III test fluid:25℃ |
% | ASTM D543 | |
Skydrol 500-A:25℃ Skydrol 500-A:25℃ |
% | ASTM D543 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Resin |
3 System |
4 Hardener |
5 60-second vertical |
6 on immersion - 24 hrs |
【新闻资讯】查看全部
海螺型材意外保持收购奇瑞新动力汽车
2016-07-15 7月12日,欲买奇瑞新能源汽车的海螺型材发布公告,鉴于奇瑞新能源汽车尚未取得新能源汽车生产资质,为此公司决定终止筹划此次重大资产重组事项。就此,历时1个月20多天的奇瑞新能源汽车上市之旅戛然而止,事情来得突然,去得突然。 有不愿具名证券分析师告诉记者,这起重组的停牌时间相比过往A股动辄3个月以上的重组案例显得有点短,并且也有点“怪”。实际上,5月30日海螺型材还对外公告称,双方同步推进独立财务顾问、审计、评估及法律顾问的遴选工作。甚至连上述中介机构都已基本确定,并推进聘请上 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |