牌号简介 About |
---|
MARPOL® LDF 724-SBV是一种醋酸乙烯共聚物树脂,专为高清晰度薄膜应用而设计。它的低熔融指数和共聚单体含量使薄膜具有优异的冲击强度、良好的热密封性和良好的低温性能。推荐应用高清晰度薄膜,共挤薄膜,泡沫,成型膜包装,密封包装,生产袋,冷冻膜,层压膜和家禽袋。 MARPOL® LDF 724-SBV is a vinyl acetate copolymer resin designed for high clarity film applications. Its low melt index and comonomer content produce films with excellent impact strength, good heat sealability and good low temperature properties. Recommended Applications High clarity films, co-extrusion films, foams, form film packaging, seal packaging, produce bags, freezer film, lamination film and poultry bags. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.5 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
4.0 | wt% | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
MD MD |
145 | MPa | ASTM D882 |
TD TD |
1720 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ASTM D1922 | |
TD TD |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
中国乙烯产业未来趋势研判
2017-06-21 世界乙烯工业已走过90多年历程。2014年,世界乙烯产能为1.53亿吨,乙烯生产装置271套,平均规模为56.5万吨/年,同比增长4.3%。世界范围内,已建和在建生产能力在100万吨/年以上的裂解装置已达40多套。美国是世界大的乙烯生产国,2014年乙烯生产能力为2842.6万吨,占世界总产能的18.5%;中国排名第二,占世界总产能的13.4%。 过去几年,中国乙烯产能和需求量均呈现增长态势,产能从2011年的1536.5万吨增至2015年的2137.5万吨,年均增幅为6. |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |