| 牌号简介 About |
|---|
| 树脂连结层是一种化学改性树脂，用于粘合不同材料，主要用于包装和工业应用。常见的粘合剂包括聚乙烯树脂和共聚物、EVA、EMA、聚丙烯、聚酰胺（尼龙）、乙烯-乙烯醇共聚物（EVOH）、离聚物和其他密封剂、聚对苯二甲酸乙二醇酯（PET）树脂和共聚物、苯乙烯聚合物、金属和纸板。产品等级主要用于吹塑和铸造薄膜、片材和热成型、吹塑、挤出涂层和层压、管材、管道和其他特殊应用，可采用颗粒形式。有关您的应用程序的更多信息和具体建议，请与您的Plexar销售和/或Equistar技术服务代表联系。 Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s). |
产品描述 Product Description
用途：包装;工业应用;
加工条件：挤出 Extrusion
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
7.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
51 | µm | |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服，51 µm，吹塑薄膜 MD, yield, 51 µ m, blow molded film |
11.0 | MPa | ASTM D882 |
|
TD，屈服，51 µm，吹塑薄膜 TD, yield, 51 µ m, blow molded film |
8.70 | MPa | ASTM D882 |
|
MD，断裂，51 µm，吹塑薄膜 MD, fracture, 51 µ m, blow molded film |
MPa | ASTM D882 | |
|
TD，断裂，51 µm，吹塑薄膜 TD, fracture, 51 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，屈服，51 µm，吹塑薄膜 MD, yield, 51 µ m, blow molded film |
% | ASTM D882 | |
|
TD，屈服，51 µm，吹塑薄膜 TD, yield, 51 µ m, blow molded film |
% | ASTM D882 | |
|
MD，断裂，51 µm，吹塑薄膜 MD, fracture, 51 µ m, blow molded film |
% | ASTM D882 | |
|
TD，断裂，51 µm，吹塑薄膜 TD, fracture, 51 µ m, blow molded film |
% | ASTM D882 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD：51 µm，吹塑薄膜 MD: 51 µ m, blow molded film |
g | ASTM D1922 | |
|
TD：51 µm，吹塑薄膜 TD: 51 µ m, blow molded film |
g | ASTM D1922 | |
|
水气透过率 Water vapor transmittance |
|||
|
100% RH，51 µm，吹塑薄膜 100% RH, 51 µ m, blow molded film |
g/m²/24 hr | ASTM F372 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
2020年涂料树脂市场规模将到达380亿美元
2016-01-06 2015-2020年涂料树脂市场每年以5.61%复合增长率增长，到2020年涂料树脂市场规模将达到380亿美元。消费者偏好绿色、环境友好和健康的涂料;以及更耐用、更好的性能和美学的涂料受到热捧，这些因素都是驱动涂料市场发展的积极因素。 丙烯酸树脂是增长最快的涂料树脂。由于它有丰富的化学特征和独特的审美属性而被应用在很多领域。目前，丙烯酸树脂的最大需求来自于汽车、医疗设备、涂料、胶粘剂及密封胶，和建设及建筑等行业。除丙烯酸、环氧和聚氨酯涂料树脂也是高增长的细分市场。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付