牌号简介 About |
---|
Kraton D1171 P是一种以苯乙烯、丁二烯和异戊二烯为基础的透明线性三嵌段共聚物,聚苯乙烯含量为19%。由北美供应,形式如下:Kraton D1171 P-作为多孔颗粒供应,Kraton D1171 P可用作热熔粘合剂的基料。也可以用作化合物配方的基础材料和沥青改性剂。 Kraton D1171 P is a clear, linear triblock copolymer based on styrene, butadiene and isoprene with a polystyrene content of 19%. Is is supplied from North America in the form below: Kraton D1171 P - supplied as a porous pellet Kraton D1171 P can be used as a base material for hot melt adhesives. It may also find use as a base material for compound formulations and as a modifier for bitumen. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D4025 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
11 | g/10min | ISO 1133 |
溶液粘度 Solution viscosity 2 |
1000 | mPa·s | 内部方法 |
结合苯乙烯 Combined with styrene |
18.1 到 21.1 | % | 内部方法 |
Antioxidant Additive Antioxidant Additive |
0.080 到 0.70 | % | 内部方法 |
Total Extractables Total Extractables |
% | 内部方法 | |
灰份含量 Ash Content |
|||
T,滑石 T. Talc |
% | 内部方法 | |
挥发物 Volatiles |
% | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,10 秒,模压成型 Shaw A, 10 seconds, molded |
ASTM D2240 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Diblock Content Diblock Content |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 25 wt% toluene solution at 25°C |
【新闻资讯】查看全部
华为在美国法院挑战FCC对中国5G技术的禁令
2020-11-06 搜料网资讯: 华为告诉美国一家上诉法院,美国联邦通信委员会(FCC)不能以国家安全问题为由阻止客户动用联邦宽带拨款来购买中国5G电信设备和服务。 华为称,FCC已超越其职权,侵 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |