| 牌号简介 About |
|---|
| 20%玻璃纤维比例的酯基注塑成型类型特点：机械强度高，低温下柔韧性好，吸音性好，着色性和印刷性好，耐热耐油，耐磨性高，易于粘合应用：鞋底、护腿板、特殊中孔。铝鞋、标准汽车应用，如：支架、热空气入口、侧门槛、换档旋钮、车顶轨、前扰流器、侧护板、手杖手柄、控制装置、农业机械和收割机的易损件、工业部件结构、外部使用的机械和摩擦高应力部件、技术具有低摩擦系数的Cal装置、杯托、中控台、溜冰滚轴芯、角色芯椅、野营用品。 Ester-based injection molding type with a ratio of 20% glass fiber Characteristics: high level of mechanical strength, good flexibility at low temperature, good noise absorption, very good colorability and printability, excellent heat & oil resistance, high abrasion resistance, easy to bond Applications: Shoe soles, shin guards, midsoles for special shoes, standard automotive applications such as: brackets, hot air intakes, side sills, shift knobs, roof rails, front spoiler, side shields, handles for walking sticks, controls, wear parts for agricultural machinery & harvester, industrial component construction, mechanical and tribologically highly stressed components in exterior use, technical units with low friction coefficients, cup holders, center console, skate roller core, role core chair, camping items. |
产品描述 Product Description
用途：室外应用;汽车领域的应用;工业应用;建筑应用领域;护栏;农业应用;安全设备;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 耐低温柔性; 耐磨; 印刷性好; 耐油; 着色性好; 耐高温; 减震; 可粘结性; Good Rigidity,noise reduction,Good Printability,High Heat Resistance,Low temperature toughness,Good wear resistance,Grease resistance,Good coloring,Agglomerability
填料：玻璃纤维 20
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.36 | g/cm³ | ISO 1183/A |
|
收缩率 Shrinkage rate |
|||
|
TD TD |
0.11 | % | |
|
MD MD |
0.49 | % | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
14 | kJ/m² | ISO 179/1eA |
|
23℃ 23℃ |
60 | kJ/m² | ISO 179/1eA |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
DIN 53752 | ||
|
MD MD |
1/℃ | DIN 53752 | |
|
TD TD |
1/℃ | DIN 53752 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
拉伸强度 tensile strength |
MPa | ISO 527-2/200 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/200 | |
|
弯曲模量 Bending modulus 2 |
ISO 178 | ||
|
-30℃ -30℃ |
MPa | ISO 178 | |
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength 3 |
ISO 178 | ||
|
-30℃ -30℃ |
MPa | ISO 178 | |
|
23℃ 23℃ |
MPa | ISO 178 | |
|
Abrasion Abrasion |
mm³ | ISO 4649 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.039 in/min |
| 3 0.079 in/min |
|
【新闻资讯】查看全部
扬子石化1-9月份共消费新产品7.16万吨
2018-10-26 加大新品开发 持续提升质量 中国石化新闻网讯 今年以来，扬子石化瞄准市场，加大新产品和专用料开发和生产力度， 1-9月份，共生产新产品7.16万吨，专用料37.27万吨，，合计增效1.4亿元。 在新产品开发方面，今年以来，扬子石化扎实抓好新产品开发工作，并取得新的突破。该公司相继开发生产了硅烷交联电缆专用料PE-LG234X 1000余吨，超高分子量聚乙烯专用料YEU 200产品350余吨，中融指高结晶聚丙烯专用料PPB-MN30-GH 470余吨，高模量聚 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付