牌号简介 About |
---|
MVR(300°C/1.2 kg)9.0 cm³/10 min;医疗设备;适用于121°C下的ETO和蒸汽灭菌;符合许多ISO 10993-1试验要求的生物相容性;中等粘度;易释放;注射成型-熔融温度280-320°C;可提供透明和不透明颜色 MVR (300 °C/1.2 kg) 9.0 cm³/10 min; medical devices; suitable for ETO and steam sterilization at 121 °C; biocompatible according to many ISO 10993-1 test requirements; medium viscosity; easy release; injection molding - melt temperature 280 - 320 °C; available in transparent and opaque colors |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.66 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
9.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD TD |
0.60 to 0.80 | % | ISO 2577 |
MD MD |
% | ISO 2577 | |
TD:2.0 mm TD:2.0 mm |
% | ISO 294-4 | |
MD:2.0 mm MD:2.0 mm |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
气体渗透 Gas permeation |
ISO 2556 | ||
二氧化碳:23℃,100.0 µm Carbon dioxide: 23 ℃, 100.0 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
氮气:23℃,100.0 µm Nitrogen: 23 ℃, 100.0 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
氧气:23℃,100.0 µm Oxygen: 23 ℃, 100.0 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 7391 | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 7391 | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 7391 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-60℃ -60℃ |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 7391 | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 7391 | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 7391 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-30℃ -30℃ |
J | ISO 6603-2 | |
23℃ 23℃ |
J | ISO 6603-2 | |
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
136℃ 136℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ISO 8302 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
Flash Ignition Temperature Flash Ignition Temperature |
℃ | ASTM D1929 | |
自燃温度 Autoignition temperature |
℃ | ASTM D1929 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
ISO 13468-2 | ||
1000 µm 1000 µm |
% | ISO 13468-2 | |
2000 µm 2000 µm |
% | ISO 13468-2 | |
3000 µm 3000 µm |
% | ISO 13468-2 | |
4000 µm 4000 µm |
% | ISO 13468-2 | |
雾度 Haze |
|||
3000 µm 3000 µm |
% | ISO 14782 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2/50 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain |
% | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Pellets |
3 60x60x2 mm, 500 bar |
4 0,079 in/min |
5 2 mm/min |
6 Based on ISO 179-1eA, 3 mm |
7 Based on ISO 180-A, 3 mm |
8 10°C/min |
9 Cross-flow |
10 程序 A |
11 方法 A |
【新闻资讯】查看全部
茂名石化成功试产高流动性低密度聚乙烯
2022-02-22 2月15日,茂名石化聚烯烃运行部 1号高压装置克服空气压缩机高负荷运行,挤压造粒机组筒体换热、颗粒水换热卡边操作等困难,成功试产高流动性低密度聚乙烯PE M1870T300吨,全部达到 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |