牌号简介 About |
---|
SABIC® LDPE 2501N0是一种没有添加剂的具有低凝胶水平的级,它结合了良好的拉伸能力和良好的光学性能和刚度。应用吹塑膜:SABIC® LDPE 2501N0通常用于尿布膜、表面保护膜、层压膜以及需要低阻塞性能且不需要存在滑动和防阻塞的应用中。铸膜:SABIC® LDPE 2501N0通常用于尿布膜、层压膜以及需要添加剂帮助的低阻塞性能应用中。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LDPE 2501N0 is a grade without additives with a low gel level, which combines good draw down ability with fair optical properties and stiffness. Application Blown Film: SABIC® LDPE 2501N0 is typically used in diaper film, surface protection film, lamination film and in applications where low blocking behaviour is required and the presence of slip and anti block is unwanted. Cast Film: SABIC® LDPE 2501N0 is typically used in diaper film, lamination film and in applications where low blocking behaviour without the help of additives is required. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.925 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.75 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
0.90 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
|||
-- -- 2 |
25 | µm | |
-- -- 3 |
50 | µm | |
弹性模量 Elastic modulus |
|||
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
MPa | ASTM D882 | |
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
MD,25 µm,铸造薄膜 MD, 25 µ m, cast thin film |
MPa | ISO 527-3 | |
TD,25 µm,铸造薄膜 TD, 25 µ m, cast thin film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
|||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ASTM D882 | |
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
|||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,25 µm,铸造薄膜 MD, fracture, 25 µ m, cast thin film |
% | ISO 527-3 | |
TD,断裂,25 µm,铸造薄膜 TD, fracture, 25 µ m, cast thin film |
% | ISO 527-3 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁冲击强度 Izod notched impact strength |
ASTM D4272 | ||
50µm,吹塑成型 50 µ m, blow molded |
J/cm | ASTM D4272 | |
铸造薄膜:25.0 µm Cast thin film: 25.0 µ m |
J/cm | ASTM D4272 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
ASTM D1003A | ||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003A | |
25 µm,铸造薄膜 25 µ m, cast thin film |
% | ASTM D1003A | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻塞力 Blocking force |
|||
吹塑薄膜,50.0 µm Blow molded film, 50.0 µ m |
g | 内部方法 | |
Re-blocking - 吹塑薄膜(50.0 µm) Re blocking - blow molded film (50.0 µ m) |
g | 内部方法 | |
撕裂强度 tear strength 3 |
ISO 6383-2 | ||
MD,50 µm MD,50 µm |
kN/m | ISO 6383-2 | |
TD,50 µm TD,50 µm |
kN/m | ISO 6383-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Cast Film |
3 Blown Film |
【新闻资讯】查看全部
生物降解材料的判定标准
2020-11-15 搜料网资讯: 可生物降解性是PBS聚酯的重要性质,目前国际上评价塑料生物降解性能的主要方法是堆肥法,堆肥中含有丰富的微生物源,能在一定程度上宏观反映塑料在自然环境中的生 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |