牌号简介 About |
---|
TOPAS 8007F-600是专为与聚乙烯(PE)共混而设计的新型挤出膜级材料。它是一种改进的透明非晶树脂,具有高硬度、防潮性、耐化学性、热成型性和纯度,适用于食品等级和一般用途。它用于铸造和吹制过程中的共混物,以及单层和多层产品。主要的薄膜应用包括扭转包装,形成腹板,保护包装,收缩膜和标签,以及容易撕裂的包装。工业用途包括成型PE和PP板材产品。为了提高性能,在高温下,建议采用更高的玻璃化转变温度(Tg)等级的TOPAS。应用于薄膜保护包装。 TOPAS® 8007F-600 Product Description TOPAS 8007F-600 is a new robust film extrusion grade designed for blending with polyethylene (PE). It is an improved clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in both cast and blown processes, and in monolayer and multilayer products. Leading film applications include twist wrap, forming webs, protective packaging, shrink films and labels, and easy tear packaging. Industrial uses include formed PE and PP sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Selected Applications Forming films (header bags, etc.) Protective packaging Shrink films and labels Twist films Decorative sheet Food packaging Food contact Leading Attributes Clarity, forming, barrier, purity, halogen-free Stiffness for downgauging, improved forming High shrink, low stress, gloss, toughness Outstanding deadfold, clean cutting Stiffness, chemical resistance, forming, even draw Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 8007F-04 - ultimate clarity extrusion grade TOPAS® 8007F-600 TOPAS® 8007F-600 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Typical application: Film. Primary characteristic: copolymer. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.01 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
1.8 | g/10min | ISO 1133 |
230℃,2.16kg 230℃,2.16kg |
10 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
190℃,2.16 kg 190℃,2.16 kg |
2.00 | cm³/10min | ISO 1133 |
230℃,2.16 kg 230℃,2.16 kg |
11.0 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
拉伸模量 Tensile modulus |
ISO 527-3/1 | ||
MD,70 µm,铸造薄膜 MD, 70 µ m, cast thin film |
MPa | ISO 527-3/1 | |
TD,70 µm,铸造薄膜 TD, 70 µ m, cast thin film |
MPa | ISO 527-3/1 | |
拉伸强度 tensile strength |
ISO 527-3/50 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3/50 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3/50 | |
拉伸应变 Tensile strain |
ISO 527-3/50 | ||
MD,断裂,70 µm,铸造薄膜 MD, fracture, 70 µ m, cast thin film |
% | ISO 527-3/50 | |
TD,断裂,70 µm,铸造薄膜 TD, fracture, 70 µ m, cast thin film |
% | ISO 527-3/50 | |
水气透过率 Water vapor transmittance |
|||
70 µm,23℃,铸造薄膜,85% RH 70 µ m, 23 ℃, cast film, 85% RH |
g·mm/m²/atm/24 hr | ASTM F1249 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,70.0 µm,铸造薄膜 60 °, 70.0 µ m, cast thin film |
ISO 2813 | ||
雾度 Haze |
|||
70.0 µm,铸造薄膜 70.0 µ m, cast thin film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 90% RH |
3 10°C/min |
【新闻资讯】查看全部
中科院最新发现PE降解酶!
2021-04-30 搜料网资讯: 日前,中科院海洋所首次发现能有效降解塑料垃圾的海洋微生物菌群和酶,两周时间可以将PE降解为碎片。 4月25日,国际学术期刊Journal of Hazardous Materials (《危险材料》) |
中科院最新发现PE降解酶! 搜料网资讯:日前,中科院海洋所首次发现能有效降解塑料垃圾的海洋微生物菌群和酶,两周时间可以将PE降解为碎片。
4月25日,国际学术期刊Journal of Hazardous Materials (《危险材料》)报道了中国科学院海洋研究所孙超岷团队最新研究成果,首次发现能有效降解聚乙烯对苯二甲酸酯和聚乙烯两种塑料的海洋微生物菌群和酶。 为获得塑料降解微生物和功能酶、发展降解塑料垃圾生物制品提供了重要理论依据和候选材料,并有望突破难降解塑料聚乙烯的降解瓶颈。 塑料是一类高分子聚合物的统称,包括聚乙烯(PE)、聚丙烯(PP)、聚乙烯对苯二甲酸酯(PET)、聚苯乙烯(PS)和聚氯乙烯(PVC)等。据报道,到2015年,人类总共生产了83亿吨塑料,其中63亿吨被废弃成为垃圾。 其大量塑料垃圾被排放进海洋。而传统塑料在自然中难以发生降解,彻底消失可能需要上百年的时间,给环境带来了巨大污染。 但实验发现,微生物经过与塑料及类似物的长期共存,逐渐演化出一些类群能有效降解塑料垃圾。孙超岷团队自2016年开始从青岛近海采集了上千份塑料垃圾,经过大量筛选发现一个塑料垃圾上附着了一个菌群,在塑料(PET和PE)表面具有很明显的定殖和降解能力。该菌群在含有塑料垃圾的培养基中能维持良好的生长能力,推测应该是通过降解塑料获得额外的能量来源。 研究人员进而结合红外光谱、凝胶渗透色谱、X射线衍射、高效液相色谱及质谱等手段多方位证实了上述菌群能有效降解PET和PE塑料。 利用宏转录组技术解析了该菌群在塑料表面通过形成生物膜定殖并分泌酶类降解利用塑料作为能量源的过程,进而筛查到多个可能参与降解PET和PE塑料的候选酶类,最终结合体外表达技术获得多个在24小时内能明显降解PE塑料的酶。 早在之前,也有科学家宣称自己创造了可在一年范围内降解的PE塑料,不过该塑料需要在制造过程中加入其它物质。英国Polymateria创造了一种一年内可降解的PE塑料。而本次研究,塑料即为普通塑料,降解塑料的菌群来自自然发现。 PE塑料目前在国际上极为缺乏能有效降解的微生物和酶类,该研究成果为下一步研究PE降解机制及发展PE降解生物制品奠定了坚实基础。目前,该研究成果已成功申请国家发明专利。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |