牌号简介 About |
---|
LD20-020C是一种经认证的主要树脂,设计用于高清晰度吹塑薄膜,用于包装要求良好光学性能的物品。LD20-020C具有膜强度、刚度、开启性好、密封性好、加工性好的最佳平衡。建议的最大薄膜降深为1.0 mil。LD20-020C含有中等滑距和中等抗滑块。LD20-020C符合FDA法规21CFR 177.1520(c)2.2和大多数与食品接触的聚乙烯使用相关的国际法规。 IROGRAN PS440-202 is a high performance polyester based thermoplastic polyurethane intended for extrusion and injection molding applications. IROGRAN PS440-202 is part of the HUNTSMAN film and sheet / technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for film and sheet, and textile laminations, polyblends, and industrial articles. PERFORMANCE FEATURES Medium hardness Tough Good low temperature properties High flexibility Wide processing window APPLICATIONS Textile lamination Polyblends Industrial articles |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.21 | g/cm³ | ASTM D792 |
密度 Density 3 |
1.21 | g/cm³ | DIN 53478 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
25 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,注塑成型 Shaw A, injection molding |
88 | ASTM D2240 | |
邵氏 A,注塑成型 Shaw A, injection molding |
DIN 53505 | ||
磨耗量 Wear amount 2 |
|||
-- -- |
mm³ | DIN 53516 | |
-- -- |
mm³ | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
断裂,0.635 mm Fracture, 0.635 mm 3 |
MPa | DIN 53504 | |
300% 应变,0.635 mm 300% strain, 0.635 mm 3 |
MPa | DIN 53504 | |
100% 应变,0.635 mm 100% strain, 0.635 mm 3 |
MPa | DIN 53504 | |
拉伸应变 Tensile strain 3 |
|||
断裂,0.635 mm Fracture, 0.635 mm 3 |
% | DIN 53504 | |
撕裂强度 tear strength 3 |
|||
0.635 mm 0.635 mm 3 |
kN/m | DIN 53515 | |
压缩形变 Compression deformation 2 |
ASTM D395 | ||
23℃,70 hr 23℃,70 hr |
% | ASTM D395 | |
70℃,24 hr 70℃,24 hr |
% | ASTM D395 | |
压缩形变 Compression deformation 2 |
DIN 53517 | ||
23℃,70 hr 23℃,70 hr |
% | DIN 53517 | |
70℃,24 hr 70℃,24 hr |
% | DIN 53517 | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TMA TMA 3 |
Internal Method | ||
High:635.0 µm High:635.0 µm |
℃ | Internal Method | |
Low:635.0 µm Low:635.0 µm |
℃ | Internal Method |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
都说废塑料回收难,难在哪里?
2018-02-09 据测算,目前我国废弃塑料年产生量一千万吨左右,再加上进口废塑料近500万吨,社会拥有量约1500万吨左右。然而,我国废旧塑料回收率却是不足25%。 但我们有没有思考过这样一个问 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |