牌号简介 About |
---|
ELITE™ 5400GS增强聚乙烯树脂是采用陶氏INSITE™技术生产的共聚物,它具有极佳的耐冲击性能,兼具优秀的抗撕裂、抗拉性能以及光学性能,可用于制造高强度的吹塑薄膜。此外ELITE™ 5400GS增强聚乙烯树脂还集合了低始封温度、较高模数和更不易阻塞等独特性能,可用于自动包装。 用途: 食品和专用包装膜。 极高的耐冲击性能。 优秀的抗撕裂、抗拉性能以及光学性能。 低始封温度、高热粘性强度,可用于制袋—充填—封口用途。 符合: 欧盟No 10/2011 法规 美国FDA FCN 424 查看法规了解完整的信息 ELITE™ 5400GS Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. It offers extremely high impact resistance, combined with excellent tear, tensile and optical properties for high strength blown film applications. In addition, ELITE 5400GS Enhanced Polyethylene Resin offers a unique combination of low seal initiation, higher modulus, and low blocking tendencies for automated packaging applications. Applications: For food and specially packaging films. Extremely high impact resistance. Excellent tear, tensile, and optical properties. Low seal initiation temperatures and high hot tack strengths for form-fill-seal applications. Complies with: EU, No 10/2011 U.S. FDA FCN 424 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.916 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
膜刺穿强度 Membrane puncture strength 2 |
|||
51 µm 51 µm 2 |
5.50 | J | 内部方法 |
膜刺穿力 Membrane puncture force 2 |
|||
51 µm 51 µm 2 |
107 | N | 内部方法 |
割线模量 Secant modulus 2 |
ASTM D882 | ||
1% 正割,MD:51 µm 1% secant, MD: 51 µ m |
MPa | ASTM D882 | |
1% 正割,TD:51 µm 1% secant, TD: 51 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength 2 |
ASTM D882 | ||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 2 |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
51 µm 51 µm 2 |
g | ASTM D1709-B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ASTM D1922 | ||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
始封温度 Initial sealing temperature 4 |
|||
51 µm 51 µm 4 |
℃ | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | DSC | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss 2 |
|||
20°,51 µm 20°,51 µm 2 |
ASTM D2457 | ||
雾度 Haze 2 |
|||
51 µm 51 µm 2 |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 在 232-246°C、2.5:1 BUR、1.9 mm 模具间隙下挤压的吹塑薄膜。 |
3 类型 A;在 232-246°C、2.5:1 BUR、1.9 mm 模具间隙下挤压的吹塑薄膜。 |
4 在 232-246°C、2.5:1 BUR、1.9 mm 模具间隙下挤压的吹塑薄膜。 实现 5.25 N/15 mm 热封强度的温度。 |
【新闻资讯】查看全部
改性塑料在家电行业的运用
2017-08-17 随着国内外家电市场的发展以及人们消费水平的提高,改性塑料在家电行业的应用越来越广泛。你家的冰箱、洗衣机、微波炉、空调、电饭煲等都出现改性塑料的身影。业内人士表示, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |