牌号简介 About |
---|
Kraton D1162P是一种基于苯乙烯和异戊二烯的透明线性三嵌段共聚物,聚苯乙烯含量为43%。它由北美提供,其物理形式如下所示。Kraton D1162 PT-作为一种粉末状致密颗粒提供,Kraton D1162 P用作粘合剂、密封剂和涂层的配料。它也可以用作沥青或热塑性塑料的改性剂和化合物配方。 SABIC® HDPE F00952J resin is a high molecular weight, high density polyethylene copolymer. The design of the product, molecular architecture and density, gives F00952J a good combination of easy extrusion and high melt strength with strong physical properties. Typical applications are thin films with excellent strength and rigidity. The material contains anti-oxidants. Typical applications SABIC® HDPE F00952J resin is typically used for blown film extrusion and production of high strength grocery sacks, shopping bags and high quality thin films for multi wall sack liners and replacement for thin paper products. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:HMW-HDPE HMW-HDPE
用途:粘合剂;复合;密封剂;涂层应用;
颜色:清晰/透明
加工条件:热成型 Thermo forming
性能特点: 嵌段共聚物; 抗氧化; Block Copolymer,Inoxidizability
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.952 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.050 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
9.5 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
15 | µm | |
弹性模量 Elastic modulus |
|||
TD,15 µm,吹塑薄膜 TD, 15 µ m, blow molded film |
1500 | MPa | ASTM D882 |
MD,15 µm,吹塑薄膜 MD, 15 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,15 µm,吹塑薄膜 MD, yield, 15 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,15 µm,吹塑薄膜 TD, yield, 15 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,15 µm,吹塑薄膜 MD, fracture, 15 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,15 µm,吹塑薄膜 TD, fracture, 15 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,15 µm,吹塑薄膜 MD, fracture, 15 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,15 µm,吹塑薄膜 TD, fracture, 15 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
15 µm,吹塑薄膜 15 µ m, blow molded film 2 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:15 µm,吹塑薄膜 MD: 15 µ m, blow molded film |
g | ASTM D1922 | |
TD:15 µm,吹塑薄膜 TD: 15 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
常温可降解!韩国亚洲大学成功开发出了一种新的PBAT材料
2022-11-18 扫描上图二维码,可以免费下载 搜料 APP 近日, 韩国亚洲 大学李分烈教授、李平天教授团队成功 开发出了一种新的PBAT材料,可以在25摄氏度下降解。 科研团队将磷酸金属盐作为催化剂 |
常温可降解!韩国亚洲大学成功开发出了一种新的PBAT材料
扫描上图二维码,可以免费下载搜料APP
近日,韩国亚洲大学李分烈教授、李平天教授团队成功开发出了一种新的PBAT材料,可以在25摄氏度下降解。科研团队将磷酸金属盐作为催化剂开发出一种新型生物降解聚合物PBAT,其制成的可降解塑料在土壤中的降解速度约是现有可降解塑料的9倍。 科研人员表示,目前大部分PBAT聚合物结构是以共价键链接形成的,只能在60℃以上、人工堆肥的条件下进行生物降解,且聚合物的分子量越大,分解速度越慢。而新型PBAT聚合物通过在生产过程中添加一定量的磷酸金属盐,使其结构变成离子键的结合形式,在保留耐久性的同时,解决了以上问题。 经测试,在室温(25℃)环境下,该新型可降解塑料在土壤中的降解速度约是现有可降解塑料的9倍。该研究成果发表在国际科学期刊《美国化学会杂志》网络版上。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。