| 牌号简介 About |
|---|
| ACRYLITE® Resist ZK-X冲击丙烯酸聚合物是一种基于聚甲基丙烯酸甲酯（PMMA）的无定形、冲击改性热塑性成型和挤出化合物。丙烯酸树脂抗冲击的典型性能有：高耐候性、高透光性、提高的抗应力开裂性、良好的熔体流动速率、易于着色。ACRYLITE® Resist ZK-X聚合物的特殊性能有：中等的抗冲击/断裂性和强度、低熔体流动速率、高耐热性，用于注塑成型件。TS和挤压板。 ACRYLITE Resist ZK-X impact acrylic polymer is an amorphous, impact-modified thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA). Typical properties of ACRYLITE Resist impact acrylic polymers are: high weather resistance high light transmission improved resistance to stress cracking good melt flow rate easy to color The special properties of ACRYLITE Resist ZK-X polymer are: medium impact/break resistance and strength low melt flow rate high heat resistance Used for injection molded parts and extruded sheet. |
产品描述 Product Description
用途：家电部件;镜头;家用货品;照明应用;文具;显示器装饰;外壳;
颜色：清晰/透明
加工条件：挤出 Extrusion
性能特点： 机械强度好; 着色性好; 耐高温; 无定形的; 透光性好; 冲击性能好; 耐候抗UV; 易流动; Good Rigidity,Weather resistance is good,Good Clarity,High impact resistance,Good liquidity,High Heat Resistance,Good coloring,Amorphous
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.16 | g/cm³ | ASTM D792 |
|
表观密度 Apparent density |
0.71 | g/cm³ | ASTM D1895 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，3.80kg 230℃，3.80kg |
1.0 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.40 to 0.70 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
平衡 balance |
< 0.30 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
0℃，6.4mm 0℃，6.4mm |
J/m | ASTM D256 | |
|
23℃，6.4mm 23℃，6.4mm |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火，6.35 mm 1.8 MPa, annealed, 6.35 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：0~100℃ MD：0~100℃ |
1/℃ | ASTM D696 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
透光率 Transmittance |
|||
|
3200 µm 3200 µm |
% | ASTM D1003 | |
|
雾度 Haze |
|||
|
3200 µm 3200 µm |
% | ASTM D1003 | |
|
黄度指数 Yellowness index |
|||
|
3.20 mm 3.20 mm |
YI | ASTM D1925 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
屈服 yield |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
采用聚氨酯拉挤材料，2022丰田Tundra复合材料座椅靠背设计获SPE汽车创新
2022-11-08 扫描上图二维码，可以免费下载 搜料 APP 巴斯夫、LLProduct、Flex-N-Gate和丰田在2022年凭借2022年丰田Tundra复合材料座椅靠背的设计获得了美国塑料工程师协会（SPE）的汽车创新奖，还在8月 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付