牌号简介 About |
---|
描述:用于热成型和片材应用的高结晶均聚物。特点:有核,侧壁刚性好,耐热性好。不含动物源性成分。加工:典型加工温度范围为450至500°F(232-260°C)。用途:分杯、冷热饮料盖、食品容器。 DESCRIPTION: High crystalline homopolymer for thermoforming and sheeting applications. FEATURES: Nucleated, excellent sidewall stiffness and heat resistance. Produced without animal derived components. PROCESSING: Typical processing temperature range of 450 to 500°F (232-260°C). APPLICATIONS: Portion cups, hot and cold beverage lids, food containers. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
2.3 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
22 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
133 | ℃ | ASTM D648 |
熔融峰值温度 Melting peak temperature |
165 to 170 | ℃ | ASTM D3418 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
正切 tangent |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
英威达运用生物基BDO开发环保氨纶
2016-06-03 碳排放限制性政策愈发收紧,市场参与者的增长也随之受限。可再生能源供应稳定,用它作为原料的产品开发似乎有更大潜力。 PTMEG和MDI是生产氨纶的两种原料,来源于石化类原料。2012年,PTMEG在氨纶中的应用比重超过70%。亚太地区是氨纶的主产地之一,PTMEG在该地的应用十分广泛。 英威达旗下一品牌Lycra(莱卡)近期将生物基氨纶应用到了面料中。这种新型纤维近70%是来自由谷物中葡萄糖所制成的可再生原料。该公司将该产品作为特种产品推入市场,销售溢价率超过 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |