| 牌号简介 About |
|---|
| ADIPRENE LF1950A是一种游离TDI含量很低的TDI端接聚酯预聚物。这种预聚物的粘度也很低，可以在较低的温度下进行加工，以获得更好的热稳定性和更长的使用寿命。当用4，4’-亚甲基双（邻氯苯胺），通常称为MBCA固化时，它会产生一种高性能，95邵尔A硬度的弹性体。ADIPRENE LF 1950A的特点是：游离TDI含量低，粘度低，使用寿命长，拆卸时间短，撕裂度和拉伸强度高。 ADIPRENE LF 1950A is a TDI-terminated polyester prepolymer having very low free TDI content. This prepolymer also has low viscosity, which allows it to be processed at reduced temperature for better heat stability and longer pot life. It yields a high performance, 95 Shore A hardness elastomer when cured with 4,4'-methylene-bis-(o-chloroaniline), commonly called MBCA. Features of ADIPRENE LF 1950A include: Low Free TDI Content Low Viscosity Long Pot Life with Short Demold Time High Tear and Tensile Strength |
产品描述 Product Description
用途：车轮;
加工条件：浇铸 casting
性能特点： 拉伸性能好; 耐磨; 机械强度好-撕裂; 低粘度; Low Viscosity,Good Tensile Strength,Good tear strength,Good wear resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.29 | g/cm³ | ASTM D792 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
裤型撕裂耐性 Pant tear resistance |
78.8 | N/mm | ASTM D1938 |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
100% 应变 100% strain |
14.5 | MPa | ASTM D412 |
|
200% 应变 200% strain |
18.6 | MPa | ASTM D412 |
|
300% 应变 300% strain |
28.3 | MPa | ASTM D412 |
|
拉伸强度 tensile strength |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D412 | |
|
撕裂强度 tear strength |
|||
|
-- -- 2 |
kN/m | ASTM D624 | |
|
开裂 cracking |
kN/m | ASTM D470 | |
|
压缩形变 Compression deformation |
|||
|
70℃，22 hr 70℃，22 hr |
% | ASTM D395B | |
|
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
储存稳定性 storage stability |
min | ||
|
脱模时间 stripping time |
min | ||
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
固化时间 Curing time |
|||
|
100℃ 100℃ |
hr | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
ASTM D2240 | ||
|
压缩强度 compressive strength |
ASTM D695 | ||
|
5% 应变 5% strain |
MPa | ASTM D695 | |
|
10% 应变 10% strain |
MPa | ASTM D695 | |
|
15% 应变 15% strain |
MPa | ASTM D695 | |
|
20% 应变 20% strain |
MPa | ASTM D695 | |
|
25% 应变 25% strain |
MPa | ASTM D695 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 C 模具 |
|
【新闻资讯】查看全部
承受850℃高灼热丝的顺德顺炎PBT工程塑料
2017-05-18 随着中国电子电器工业的迅速发展，人们对电子电器产品的安全性能日益重视，对于高灼热丝性能阻燃增强工程塑料的需求日益增长。顺炎新材的一种“850℃灼热丝不起燃的阻燃增强PBT塑料及其制备方法”已经获得国家发明专利，并在CHINAPLAS 2017亮相。 PBT工程塑料广泛应用于电子电器元件中，如接插件、变压器、熔断器外壳、开关、继电器、节能灯、线圈骨架、连接器等。电子电器中的塑料元件在过载、短路、漏电等情况下会造成局部过热并可能引起燃烧，因此，必须降低塑料元件的着火危险程度。其 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付