牌号简介 About |
---|
Ultramid® A3HG7是一种35%玻璃纤维增强注塑成型PA66级。典型应用包括高刚度和尺寸稳定性的机械部件和外壳,如齿轮、电磁阀外壳、电流量加热器、拖曳电缆附件以及电绝缘部件。 Ultramid A3HG7 is a 35% glass fiber reinforced injection molding PA66 grade. Applications Typical applications include machinery components and housings of high stiffness and dimensional stability such as gears, solenoid valve housings, electrical flow heaters, trailing cable attachments, as well as electrically insulating parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.42 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD MD |
0.30 | % | ISO 294-4 |
TD TD |
0.50 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.60 | % | ISO 62 |
饱和,23℃ (23°C, 饱和) |
4.5 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲强度 bending strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 178 | |
屈服,90℃ Yield, 90 ℃ |
MPa | ISO 178 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306/A50 | |
A50 A50 |
℃ | ISO 306 | |
最大使用温度 Maximum operating temperature |
℃ | IEC 216 | |
球压测试 Ball pressure test |
|||
耐热 heat-resisting |
IEC 309 | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
绝缘强度 Insulation strength |
|||
2.00mm 2.00mm |
KV/mm | IEC 60243-1 | |
耗散因数 Dissipation factor |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.40 mm 0.40 mm |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
灼热丝相对温度 Relative temperature of heating wire |
|||
0.80mm 0.80mm |
℃ | IEC 60695-2-13 | |
3.20mm 3.20mm |
℃ | IEC 60695-2-13 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
输油管线遭黑客攻击关停,美国多地进入紧急状态
2021-05-11 搜料网资讯: 美国政府9日宣布,17个州和华盛顿特区进入紧急状态。原因是美国最大的燃油输送管线遭遇网络攻击被迫关停,这导致美国东海岸45%的汽油、柴油等燃料供应受到影响,具 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |