Novalloy-B B5503是一种丙烯腈丁二烯苯乙烯 + PBT (ABS+PBT)产品,含有的填充物为15% 玻璃纤维增强材料。 它可以通过注射成型或涂层进行加工,在北美洲有供货。 Novalloy-B B5503的应用领域包括电气/电子应用、商业/办公用品、房屋 和 涂覆应用。 特性包括: 阻燃/额定火焰 Flame Retardant 耐化学品 耐磨 加工性能良好 Novalloy-B B5503 is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) product filled with 15% glass fiber. It can be processed by coating or injection molding and is available in North America. Applications of Novalloy-B B5503 include electrical/electronic applications, business/office goods, coating applications and housings. Characteristics include: Flame Rated Chemical Resistant Flame Retardant Wear Resistant Good Adhesion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.38 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.30 到 0.50 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.15 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
88.3 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
2.7 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,6.35 mm 0.45 MPa, unannealed, 6.35 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.35 mm 1.8 MPa, unannealed, 6.35 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance |
|||
3.18 mm 3.18 mm |
sec | ASTM D495 | |
相比耐漏电起痕指数 Compared to the resistance to leakage and marking index |
|||
3.18 mm 3.18 mm |
V | UL 746 | |
高电弧燃烧指数(HAI)(1.59 mm) High Arc Burning Index (HAI) (1.59 mm) |
UL 746 | ||
高电压电弧起痕速率(HVTR)(1.59 mm) High voltage arc marking rate (HVTR) (1.59 mm) |
mm/min | UL 746 | |
热丝引燃(HWI)(1.59 mm) Hot wire ignition (HWI) (1.59 mm) |
sec | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.50 mm,所有颜色 1.50 mm, all colors |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
十年“限塑令”效果遭疑 治理白色污染前路如何?
2018-01-19 近期,国家发改委向社会征集塑料垃圾污染防治的建议,“限塑令”发布十年后,中国治理“白色污染”的成效再度引发舆论热议。 一方面是社会对“限塑令”效果的质疑,一方面是快递、外卖等新业态对塑料包装的刚需,中国与“白色污染”的拉锯战前路如何? 发改委:正研究制定防治塑料垃圾污染的政策 近日,国家发改委网站发布《我为塑料垃圾污染防治建言献策》的消息,邀请社会各界围绕不同领域塑料制品的管理要求,提出意见建议。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |