牌号简介 About |
---|
AClar 33C(0.75 mil)是一种主要由三氟氯乙烯(CTFE)组成的共聚物膜。它可以在压力成型机和真空成型机上进行热成型。 Aclar 33C (0.75 mil) is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is thermoformable on both pressure and vacuum forming machines. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.12 | g/cm³ | ASTM D1505 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
MD:19 µm MD:19 µm |
1660 | MPa | ASTM D882 |
TD:19 µm TD:19 µm |
1450 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,19 µm MD, yield, 19 µ m |
83.0 | MPa | ASTM D882 |
TD,屈服,19 µm TD, yield, 19 µ m |
27.6 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,屈服,19 µm MD, yield, 19 µ m |
% | ASTM D882 | |
TD,屈服,19 µm TD, yield, 19 µ m |
% | ASTM D882 | |
水气透过率 Water vapor transmittance |
|||
19 µm,38℃,100% RH 19 µm,38℃,100% RH |
g·mm/m²/atm/24 hr | ASTM F1249 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | ASTM D3418 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
19.1 µm 19.1 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |