牌号简介 About |
---|
AvaSpire AV-621 GF30是AvaSpire AV-621的 30%玻纤增强牌号。该配方比30% 玻纤增强PEEK具有更好的尺寸稳定性和更低的翘曲。该树脂保持了玻纤增强PEEK大多数有用的超高性能,包括耐化学性、耐疲劳性,长期热氧化稳定性,但热变形温度低于30%碳纤增强PEEK。 该材料在各种性能之间取得的优异平衡使之非常适合包括医疗保健、交通运输、电子、石油和天然气、化学处理等要求苛刻的各类行业。 -米色: AV-621 GF30 BG 20 -黑色:AV-621 GF30 BK95 AvaSpire® AV-621 GF30 is a 30% glass fiber reinforced version of AvaSpire® AV-621. This formulation offers better dimensional stability and lower warpage than 30% glass reinforced PEEK. This resin retains most of the desirable ultra-performance attributes of glass reinforced PEEK, including chemical resistance, fatigue resistance and long term thermal oxidative stability, but the heat deflection temperature is lower than 30% GF PEEK. The material's excellent balance of properties makes it well suited for demanding applications across a broad range of industries including healthcare, transportation, electronics, oil and gas, and chemical processing. Beige: AV-621 GF30 BG 20 Black: AV-621 GF30 BK 95 |
产品描述 Product Description
厂家:比利时索尔维 Solvay
类别:PAEK PAEK
用途:医疗/护理用品;医疗器械;工业应用;
颜色:黑色,米黄色
加工条件:型材挤出成型 Profile extrusion
性能特点: 防火阻燃等级V-1; 防火阻燃等级V-0; 机械强度好; 尺寸稳定性好; 耐化学性; 耐疲劳性好; 耐高温; 阻燃; Good Rigidity,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Fatigue resistance,Solvent resistance,V-1,V-0
填料:玻璃纤维 30
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-- -- |
120 | J/m | ASTM D256 |
-- -- |
14 | kJ/m² | ISO 180 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-- -- |
1000 | J/m | ASTM D4812 |
-- -- |
70 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
217 | ℃ | ASTM D648 |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-50~50℃ MD:-50~50℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
DSC | ||
50℃ 50℃ |
J/kg/℃ | DSC | |
200℃ 200℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3 mm 3 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- 5 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/5 | |
-- -- 5 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/1A/5 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
泊松比 Poisson's ratio |
ASTM E132 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
熔体质量流动速率 Melt Flow Rate |
|||
400℃,2.16kg 400℃,2.16kg |
g/10min | ASTM D1238 | |
收缩率 Shrinkage rate 4 |
ASTM D955 | ||
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃,1000 sec^-1 400℃,1000 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 Only AvaSpire® AV-621 BG20 is ISO 10993 certified |
2 一般属性:这些不能被视为规格。 |
3 5" x 0.5" x 0.125" bars |
4 0.20 in/min |
【新闻资讯】查看全部
十建古雷炼化项目全力推进乙烯“双塔”模块化施工
2021-04-21 搜料网资讯: 近日,炼化工程十建公司承建的古雷炼化一体化项目80万吨/年乙烯装置急冷水塔和急冷油塔分别于10月11日和15日陆续进厂,两台塔器模块化预制工作立即展开,项目部迅速 |
十建古雷炼化项目全力推进乙烯“双塔”模块化施工 搜料网资讯:近日,炼化工程十建公司承建的古雷炼化一体化项目80万吨/年乙烯装置急冷水塔和急冷油塔分别于10月11日和15日陆续进厂,两台塔器模块化预制工作立即展开,项目部迅速掀起劳动竞赛施工高潮。 急冷油塔作为古雷炼化一体化项目中使用4000吨吊车吊装的首台设备,业主、总包、十建公司三方密切配合,及时落实设备进厂时间,对模块化施工、吊装等方案进行科学组织、周密部署,为急冷油塔的按时吊装创造有利条件。急冷油塔计划于11月2日开始进行吊装。面对紧迫的施工工期,项目部提高参建员工紧迫意识,调动其工作积极性,项目部定时间、定节点、定目标,实行责任到人、责任到岗,组织参建人员加班加点,安全、高效推进塔器设备模块化施工进程,确保实现项目“首吊”目标。 在塔器设备模块化施工的同时,4000吨大吊车组装工作陆续展开。项目部每天组织塔器模块化施工现场协调会,对一天施工进行汇报、总结,会上当场解决施工队反馈的问题,为施工单位创造最有利的作业条件。项目部通过投用全位置自动焊、新型盘扣式脚手架等先进工装,提升了塔器模块化施工效率,为实现首台大型设备“穿衣戴帽、塔起灯亮”的目标打下坚实基础。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。