SuMulthein PR-103I是一种具有短凝胶时间和高反应性树脂的直型酚醛清漆型粉末。特性:苏木精PR-103I为粉末状酚醛树脂,六胺含量约11%,分子量中等。摩擦:可减少热成型和后固化工艺,提高胶芯的硬度:固化时间短,最好与有机溶剂或液体油混合。 SUMILITERESIN® PR-103 I is a straight novolak type powder with short gel time and high reactive resin. Characteristics SUMILITERESIN® PR-103 I is powder novolac phenolic resin with hexamine contained about 11% and middle molecular number. For Friction : hot molding and post curing process can be reduced and improve Hardness For Adhesive core : short cure and preferable mix with organic solvent or liquid oil. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Flow Length(125℃) Flow Length(125℃) |
2.00 到 4.00 | cm | |
颗粒大小分布 Particle size distribution |
|||
106μm 106μm |
< 5.0 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
98.0 到 107 | ℃ | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
胶凝时间 Gelation time |
|||
150℃ 150℃ |
0.83 到 1.3 | min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中国智能协作机器人产业将迎来全新格局
2021-03-28 搜料网资讯: 近日,湖南瑞森可机器人科技有限公司与美国Rethink Robotics公司、长沙市政府达成战略合作,将世界领先的智能协作机器人引入中国,并将相关产品的首批生产基地落户长沙 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |