牌号简介 About |
---|
PRE-ELEC® PBT 1455是一种基于PBT的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。PRE-ELEC® PBT 1455具有优良的机械性能和良好的化学和耐磨性。典型应用包括用于爆炸性环境区域的注塑技术零件。Pre-elec PBT 1455适用于要求PBT具有良好机械性能的应用场合。 PRE-ELEC® PBT 1455 is a conductive thermoplastic compound based on PBT. Conductivity is achieved by using special conductive carbon black. PRE-ELEC PBT 1455 has excellent mechanical properties as well as good chemical and wear resistance. Typical applications include injection moulded technical parts for areas with explosive atmosphere. PRE- ELEC® PBT 1455 is ideal for the applications where the good mechanical properties of PBT are required. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.33 | g/cm³ | ASTM D792 |
密度 Density |
1.32 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
240℃,10.0kg 240℃,10.0kg |
14 | g/10min | ASTM D1238 |
240℃,21.6kg 240℃,21.6kg |
60 | g/10min | ASTM D1238 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
240℃,10.0kg 240℃,10.0kg |
14 | g/10min | ISO 1133 |
240℃,21.6kg 240℃,21.6kg |
g/10min | ISO 1133 | |
收缩率 Shrinkage rate |
|||
MD MD |
% | ASTM D955 | |
MD MD |
% | ISO 294-4 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
4 mm 4 mm |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,4 mm Fracture, 4 mm |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
4 mm 4 mm |
MPa | ASTM D790 | |
4 mm 4 mm |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 2 |
|||
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ASTM D256 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 2 |
|||
-20℃ -20℃ |
ASTM D256 | ||
-20℃ -20℃ |
ISO 179 | ||
23℃ 23℃ |
ISO 179 | ||
23℃ 23℃ |
ASTM D256 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 2 |
ISO 180 | ||
Area Area |
ASTM D256 | ||
-20℃,4.00 mm -20℃,4.00 mm |
ASTM D256 | ||
23℃,4.00 mm 23℃,4.00 mm |
ASTM D256 | ||
-20℃ -20℃ |
ISO 180 | ||
23℃ 23℃ |
ISO 180 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
-20℃,4 mm -20℃,4 mm |
ASTM D256 | ||
23℃,4 mm 23℃,4 mm |
ASTM D256 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 2 |
ISO 180 | ||
-20℃ -20℃ |
ISO 180 | ||
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648-A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 3 | |
-- -- |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4 mm thickness |
3 标准 B (120°C/h), 载荷2 (50N) |
4 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
达能公司已将采用可再应用或可堆肥的资料包装
2018-10-30 达能公司已宣布,到2025年其包装将采用100%可回收、可再利用或可堆肥的材料制成,并试图帮助发展回收基础设施,以提高回收率。 公司已经设定了三个目标来实现向循环经济的转变:改进产品的设计;在包装中加入更 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |