牌号简介 About |
---|
Cycoloy CX7240U树脂CYCOLOY™ CX7240U resin是一种可注射成型的PC/ABS混合物,带有紫外线稳定包装。它包含无溴和无氯阻燃系统,以满足薄壁阻燃。卓越的流动和冲击平衡,加上薄壁阻燃性和所有颜色选项,使Cycoloy CX7240U成为各种薄壁应用的理想选择。 CYCOLOY CX7240U Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is an enhanced performance & processability with UV stabilized grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VA/B flame rating. CYCOLOY CX7240U resin is an excellent candidate for a wide variety of thin wall applications including enclosures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,2.16kg 260℃,2.16kg |
16 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,2.16 kg 260℃,2.16 kg |
15.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.40 to 0.60 | % | 内部方法 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Af | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
75℃ 75℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.40 mm 0.40 mm |
UL 94 | ||
0.60 mm 0.60 mm |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 80*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
PE供给结构失衡 HDPE强势下跌
2017-12-15 下半年以来,管材-低压膜-中空-注塑和拉丝先后开启了上涨行情。其中涨幅最大的是中空,涨幅高达2400元/吨,其次是低压膜上涨了2300元/吨。通过分析低压的基本面发现,今年需求面整体波动不大,而供应面给予行情支撑力度较强。国产和进口资源在产品结构和供应量两方面的综合作用,致使下半年低压资源供应不足。 如果说去年市场的明星产品是高压,那么今年低压各类品种的表现可谓非常抢眼。今年低压市场整体延续了去年“上半年跌,下半年涨”的态势。下半年以来,管材-低压膜-中空-注塑和拉丝先后开 |
PE供给结构失衡 HDPE强势下跌 第三季度至今,管材-低压膜-中空-注塑加工和金属拉丝依次打开了上涨市场行情。在其中涨幅较大的是中空,涨幅达到2400元/吨,次之是低压膜上涨了2300元/吨。根据剖析低压的股票基本面发觉,2020年需求面总体起伏并不大,而供应面给与市场行情支撑点幅度较强。国内和進口資源在产品品种和供应量两层面的综合性功效,导致第三季度低压資源供应不够。 假如说上年销售市场的主打产品是髙压,那麼2020年低压各种种类的主要表现可以说十分引人注意。2020年低压销售市场总体持续了上年“上半年度跌,第三季度涨”的趋势。第三季度至今,管材-低压膜-中空-注塑加工和金属拉丝依次打开了上涨市场行情,在其中低压注塑加工与上年类似,进到11月份后大幅度上涨,涨幅与上年非常,别的四类低压商品的涨幅远超上年。据调查,自6月份至今,涨幅较大的是中空,涨幅达到2400元/吨,次之是低压膜上涨了2300元/吨,低压注塑加工和低压管材各自上涨了2000元/吨和1700元/吨,金属拉丝市场行情起动比较晚,现阶段看来涨幅在750元/吨。(备注名称:价钱选择的是上海市场12月11日与六月份的价格比较) 根据剖析低压的股票基本面发觉,2020年低压需求面总体起伏并不大,而供应面给与市场行情支撑点幅度较强。国内和進口資源在产品品种和供应量两层面的综合性功效,导致第三季度低压資源供应不够。现阶段中国低压商品的产出率在52%上下,这篇暂以国产资源来关键剖析,進口資源将在事后文章内容中展现。 从低压月度总结生产量看来,除开低压管材生产量慢慢上涨以外,别的种类第三季度商品均有下降。特别是在11月份HDPE中空和注塑加工国生产量大幅度下降,同比减缩了53%和38%,导致销售市场这两类商品出現了显著的上涨,目前为止国内中空价钱已涨至11600-1240零元/吨不一,国内注塑加工涨至10300-1160零元/吨不一,全国各地資源都比较焦虑不安。低压金属拉丝尽管从生产量看来,总体起伏力度比较有限,但中国低压金属拉丝的生产商关键以兰州石化、大庆石化和抚顺石化主导,年末受气温极端和运输能力不够的牵制,货品配制亦遭受危害,从而导致销售市场供应稍显不畅。 从低压产品品种看来,2020年低压管材生产制造占较为大,在31%。关键受海绵城市建设基本建设和煤改电等现行政策的利好消息,2020年中下游管材要求还行,原材料价格亦首先上涨。在确保生产制造经济效益较大的状况下,制造业企业在商品排产层面,向低压管材歪斜,因而导致别的低压种类力度相对减缩。 总的来说,供应焦虑不安给与2020年低压市场行情极强的支撑点,但供求的不断失衡也给供应公司明确提出了高些的规定。在中国PE生产能力持续提高的情况下,总体看来在我国PE自给自足工作能力进一步提高,但产品品种仍需健全。也必须生产制造行为主体提升各中下游市场细分的科学研究,以做到商品供应健全有效,供求身心健康稳定。 来源于:变宝网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。