牌号简介 About |
---|
HE125Mo是一种用于注塑成型的聚丙烯均聚物。该牌号具有流动性好、刚度高的特点,特别适用于要求易流动的制品的高速注塑成型。它非常好的感官性能使这种等级可以用于任何母粒,而不会变色问题。 HE125MO is a polypropylene homopolymer intended for injection moulding. This grade is characterized by good flow properties and high stiffness in and is specially suitable for high-speed injection moulding of articles demanding easy flow. Its very good organoleptic properties allows this grade to be used with any masterbatch without discoloring problems. Applications House ware and thin wall packaging Articles with rather long and narrow flow lengths Special Features Good flow behaviour High stiffness |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.908 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
12 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
1.0 to 2.0 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
3.5 | kJ/m² | ISO 179/1eA |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 1 |
|||
0.45 MPa,未退火 0.45 MPa, unannealed 1 |
88.0 | ℃ | ISO 75-2/B |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/50 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Injection molded specimen |
【新闻资讯】查看全部
亨内基推出注塑成型的疾速PU彩涂更换零碎
2017-12-27 亨内基已经引进了一条机器生产线,在涂层注塑成型组件时可以处理颜色磨损并快速更换颜色。 这种被称为Color Line Multi-Connect的即插即用系统可以进行表层铸型并且用聚氨酯和聚脲快速干净的变色。 亨内基表示新机器可以使用“聚氨酯彩涂系统注入注塑成型零件。通过使用不同的颜色和颜料效果,如金属片,并且几乎不会产生设计缺陷。” |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |