洛塔德HX8290是一种乙烯、丙烯酸酯和马来酸酐的无规三元共聚物,经高压釜聚合而成。由于其性能、反应性、流动性和与增粘树脂和蜡的相容性,洛塔德HX8290适用于热熔胶配方的添加剂,也适用于无卤阻燃电线电缆等矿物填充的偶联剂。 LOTADER® HX8290 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process. Applications Due to its properties, reactivity, fluidity and compatibility with tackifying resins and waxes, LOTADER ® HX8290 is suitable as additive for hot melt adhesive formulations and as coupling agent in mineral filled compounds such as halogen free flame retardant wires and cables. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D1505 |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
70 | g/10min | ISO 1133 |
190℃,2.16kg 190℃,2.16kg |
70 | g/10min | ASTM D1238 |
丙烯酸乙酯含量 Ethyl acrylate content |
17.0 | wt% | |
马来酸酐含量 Maleic anhydride content |
wt% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
MPa | ISO 527-2 | |
断裂,模压成型 Fracture, molded |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ASTM D638 | |
断裂,模压成型 Fracture, molded |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
模压成型 Compression Molding |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
断供!停产!日均倒闭400家企业!这里按下暂停键…
2021-10-18 搜料网资讯: 越南是全球产业链、供应链中的重要一环,然而新冠疫情的持续蔓延,对当地制造业造成严重冲击。为尽快恢复经济,越南于本月初解除了制造业发达的胡志明市及周边地 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |