牌号简介 About |
---|
MVR(300°C/1.2 kg)13 cm³/10分钟;LED照明、光学和透镜;传输率最高的PC;中等粘度;紫外线稳定;注塑-熔融温度280-320°C;仅提供颜色代码551053 MVR (300 °C/1.2 kg) 13 cm³/10 min; LED Lighting, optics and lenses; PC with highest transmission; medium viscosity; UV stabilized; injection molding - melt temperature 280 - 320 °C; available in color code 551053 only |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:PC Polycarbonate
用途:镜头;照明应用;光学应用;发光二极管;
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 防火阻燃等级V-2; 透光性好; 耐候抗UV; HB,V-2,Weather resistance is good,Good Clarity
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.66 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
13 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
13.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD TD |
0.60 to 0.80 | % | ISO 2577 |
MD MD |
% | ISO 2577 | |
TD:2.0 mm TD:2.0 mm |
% | ISO 294-4 | |
MD:2.0 mm MD:2.0 mm |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
气体渗透 Gas permeation |
ISO 2556 | ||
二氧化碳:23℃,100.0 µm Carbon dioxide: 23 ℃, 100.0 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
氮气:23℃,100.0 µm Nitrogen: 23 ℃, 100.0 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
氧气:23℃,100.0 µm Oxygen: 23 ℃, 100.0 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 7391 | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 7391 | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 7391 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-60℃ -60℃ |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 7391 | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 7391 | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 7391 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-30℃ -30℃ |
J | ISO 6603-2 | |
23℃ 23℃ |
J | ISO 6603-2 | |
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
138℃ 138℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ISO 8302 | |
相对温度指数 Relative temperature index |
|||
电气性能,1.50 mm Electrical performance, 1.50 mm |
℃ | UL 746 | |
强度机械性能,1.50 mm Strength mechanical performance, 1.50 mm |
℃ | UL 746 | |
冲击机械性能,1.50 mm Impact mechanical performance, 1.50 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
2.50 mm 2.50 mm |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
燃烧速率 Burning rate |
|||
USFMVSS,> 1.00 mm USFMVSS,> 1.00 mm |
ISO 3795 | ||
Flash Ignition Temperature Flash Ignition Temperature |
℃ | ASTM D1929 | |
自燃温度 Autoignition temperature |
℃ | ASTM D1929 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
ISO 13468-2 | ||
1000 µm 1000 µm |
% | ISO 13468-2 | |
2000 µm 2000 µm |
% | ISO 13468-2 | |
3000 µm 3000 µm |
% | ISO 13468-2 | |
4000 µm 4000 µm |
% | ISO 13468-2 | |
雾度 Haze |
|||
3000 µm 3000 µm |
% | ISO 14782 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain |
% | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Pellets |
3 60x60x2 mm, 500 bar |
4 0.079 in/min |
5 2 mm/min |
6 Based on ISO 179-1eA, 3 mm |
7 Based on ISO 180-A, 3 mm |
8 10°C/min |
9 Cross-flow |
10 程序 A |
11 方法 A |
【新闻资讯】查看全部
投资1亿欧元!日本东丽推动在欧洲的碳纤维投资,满足新交通、可再生
2022-12-07 扫描上图二维码,可以免费下载 搜料 APP 东丽碳纤维欧洲公司,欧洲市场领导者将投资约1亿欧元(1.04亿美元),在其位于法国西南部的工厂建设一条新生产线。这项投资将使该公司能够满 |
投资1亿欧元!日本东丽推动在欧洲的碳纤维投资,满足新交通、可再生
扫描上图二维码,可以免费下载搜料APP
东丽碳纤维欧洲公司,欧洲市场领导者将投资约1亿欧元(1.04亿美元),在其位于法国西南部的工厂建设一条新生产线。这项投资将使该公司能够满足法国和其他欧洲国家对高性能碳纤维日益增长的需求。
该公司表示,新的生产线将能够生产一系列具有优异机械性能的碳纤维。这些优质产品满足了新交通、可再生能源、核电、航空航天等高科技行业的要求。 该项目将于2023年下半年启动,预计将于2025年底投产。这项投资将提供高达1000吨/年的额外产能,还将为工厂创造约50个新工作岗位。 东丽碳纤维欧洲首席执行官Jean-Marc Guilhempey强调表示: “这笔投资表明了我们的股东对我们产品卓越的认可,以及他们对我们公司的信心。这也将使我们能够加强和确保我们在法国的专业性。” 自2019冠状病毒病(COVID-19)大流行以来,东丽碳纤维欧洲公司调整了其商业模式,从专注于航空航天市场转向与绿色能源生产和新型移动解决方案开发相关的工业部门。鉴于这些新兴行业的持续需求以及航空航天行业的逐步复苏,东丽碳纤维欧洲公司认为,现在就开始投资并为未来做好准备至关重要。 早些时候,东丽宣布将在美国投资1500万美元,将其高性能Torayca T1100碳纤维的产能提高一倍,并在迪凯特增加关键冗余。此次升级是为了响应美国国防应用需求的增长,显著提高Torayca T1100下一代中间模加(IM+)碳纤维的可用性和缩短交付时间。这种材料是美国国防部几种武器系统的关键部件,也是未来垂直升降(FVL)平台的结构应用。 东丽是美国最大的碳纤维制造商,拥有完整的供应链。迪凯特工厂拥有从前驱体到碳纤维的生产线,是东丽三大制造工厂之一。该公司在华盛顿州的塔科马市和南卡罗来纳州的斯帕坦堡都设有生产前驱体、碳纤维和预浸料的工厂。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- LED聚光灯
- 2019-04-08 0
- Makrolon® LED2643是一种注塑级的聚碳酸酯(PC)这种材料是专门为固态照明灯具(SSL)开发的。它的特点是特别高的传输和非常好的抵抗发光二级管发出的光。
- 阅读全文
LED聚光灯
1-Makrolon® LED2643是一种注塑级的聚碳酸酯(PC)
2-MVR(300°C/1.2 kg),13.0 cm³/10 min
3-拉伸模量(23℃),2350MPa
4-简支梁缺口冲击强度(23℃,局部断裂),70.0kJ/m²
2-MVR(300°C/1.2 kg),13.0 cm³/10 min
3-拉伸模量(23℃),2350MPa
4-简支梁缺口冲击强度(23℃,局部断裂),70.0kJ/m²
潜在的成本和节能使LED(发光二极管)成为比其他照明技术更明智的选择,用于室内外照明应用。拜耳位于奥地利维也纳分公司的创新性立面照明被LED聚光灯取代。Carclo光学公司使用Makrolon®LED2643为本项目制造透镜。这种材料是专门为固态照明灯具(SSL)开发的。它的特点是特别高的传输和非常好的抵抗发光二级管发出的光。
收起
- LED光源透镜
- 2019-01-25 0
- Makrolon® LED2643为中等粘度、紫外线稳定性好的聚碳酸酯树脂PC,注塑-熔融温度280-320°C
- 阅读全文
LED光源透镜
1-Makrolon® LED2643为中等粘度、紫外线稳定性好的聚碳酸酯树脂PC
2-熔体质量流动速率(300℃,1.20kg) 13 g/10min
3-收缩率(TD) 0.60-0.80 %
4-拉伸模量(23℃) 2350 MPa
5-弯曲模量(23℃) 2350 MPa
6-简支梁无缺口冲击强度(-60℃) 无断裂
7-热变形温度(1.8 MPa,未退火) 126 ℃
8-阻燃等级(0.75 mm) V-2
2-熔体质量流动速率(300℃,1.20kg) 13 g/10min
3-收缩率(TD) 0.60-0.80 %
4-拉伸模量(23℃) 2350 MPa
5-弯曲模量(23℃) 2350 MPa
6-简支梁无缺口冲击强度(-60℃) 无断裂
7-热变形温度(1.8 MPa,未退火) 126 ℃
8-阻燃等级(0.75 mm) V-2
收起