牌号简介 About |
---|
Vibrathane B892是一种以TDI封端的聚醚基预聚物。预聚物是室温下的液体。当用MBCA固化时,Vibrathane B892生成91邵尔A硬度聚氨酯。 VIBRATHANE B892 is a TDI terminated, polyether based prepolymer. The prepolymer is a liquid at room temperature. VIBRATHANE B892 yields a 91 Shore A hardness urethane when cured with MBCA. |
技术参数 Technical Data | |||
---|---|---|---|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变 100% strain |
7.38 | MPa | ASTM D412 |
300% 应变 300% strain |
14.2 | MPa | ASTM D412 |
拉伸强度 tensile strength |
27.6 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
400 | % | ASTM D412 |
撕裂强度 tear strength |
|||
-- -- 2 |
86.3 | kN/m | ASTM D624 |
开裂 cracking |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
储存稳定性 storage stability |
min | ||
脱模时间 stripping time |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
压缩强度 compressive strength |
ASTM D695 | ||
5% 应变 5% strain |
MPa | ASTM D695 | |
10% 应变 10% strain |
MPa | ASTM D695 | |
15% 应变 15% strain |
MPa | ASTM D695 | |
20% 应变 20% strain |
MPa | ASTM D695 | |
25% 应变 25% strain |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
格林循环拟募资9.37亿元投入年循环再生10万吨改性塑料等项目
2021-07-30 搜料网资讯: 格林美7月25日晚间公告,控股子公司江西格林循环产业股份有限公司(下称格林循环)首次公开发行股票并在创业板上市申请,获深交所受理。 招股书显示,格林循环拟募 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |