牌号简介 About |
---|
己烯线性低密度树脂槽铸挤压突出的下拉能力符合美国FDA 21 CFR 177.1520(c)3.1a有关完整的详细信息,请参考法规。TUFLIN™ HS-7046 NT 7线性低密度聚乙烯树脂是一种乙烯-己烯共聚物,线性低密度(LLDPE)树脂设计用于槽铸挤出。本产品推荐用于要求透明性和高韧性的槽铸薄膜应用,作为共挤结构的核心层。 Hexene Linear Low Density Resin Slot Cast Extrusion Outstanding Drawdown Capability Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a Consult the regulations for complete details. TUFLIN™ HS-7046 NT 7 Linear Low Density Polyethylene Resin is an ethylene-hexene copolymer, linear low density (LLDPE) resin designed for slot cast extrusion. This product is recommended for slot cast thin film applications requiring both clarity and superior toughness as the core layer in coextruded structures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
膜刺穿强度 Membrane puncture strength |
内部方法 | ||
20 µm 20 µm |
4.63 | J | 内部方法 |
51 µm 51 µm |
6.78 | J | 内部方法 |
膜刺穿力 Membrane puncture force |
内部方法 | ||
20 µm 20 µm |
53.4 | N | 内部方法 |
51 µm 51 µm |
N | 内部方法 | |
膜耐刺穿性 Membrane puncture resistance |
内部方法 | ||
20 µm 20 µm |
J/cm³ | 内部方法 | |
51 µm 51 µm |
J/cm³ | 内部方法 | |
膜强度 Membrane strength |
ASTM D882 | ||
MD:20 µm MD:20 µm |
J/cm³ | ASTM D882 | |
MD:51 µm MD:51 µm |
J/cm³ | ASTM D882 | |
TD:20 µm TD:20 µm |
J/cm³ | ASTM D882 | |
TD:51 µm TD:51 µm |
J/cm³ | ASTM D882 | |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:20 µm 2% secant, MD: 20 µ m |
MPa | ASTM D882 | |
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
MPa | ASTM D882 | |
2% 正割,TD:20 µm 2% secant, TD: 20 µ m |
MPa | ASTM D882 | |
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,20 µm MD, yield, 20 µ m |
MPa | ASTM D882 | |
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,20 µm TD, yield, 20 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,20 µm MD, fracture, 20 µ m |
MPa | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
落锤冲击 Gardner Impact |
|||
20 µm 20 µm |
g | ASTM D1709-A | |
20 µm 20 µm |
g | ASTM D1709-B | |
51 µm 51 µm |
g | ASTM D1709-A | |
51 µm 51 µm |
g | ASTM D1709-B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 2 |
ASTM D1922 | ||
MD:20 µm MD:20 µm |
g | ASTM D1922 | |
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:20 µm TD:20 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
始封温度 Initial sealing temperature 3 |
内部方法 | ||
20 µm 20 µm |
℃ | 内部方法 | |
51 µm 51 µm |
℃ | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
20°,20.3 µm 20°,20.3 µm |
ASTM D2457 | ||
20°,50.8 µm 20°,50.8 µm |
ASTM D2457 | ||
45°,20.3 µm 45°,20.3 µm |
ASTM D2457 | ||
45°,50.8 µm 45°,50.8 µm |
ASTM D2457 | ||
雾度 Haze |
ASTM D1003 | ||
20.3 µm 20.3 µm |
% | ASTM D1003 | |
50.8 µm 50.8 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密封强调 Sealing emphasis 4 |
内部方法 | ||
130℃,20.3 µm 130℃,20.3 µm |
g | 内部方法 | |
150℃,50.8 µm 150℃,50.8 µm |
g | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 B |
3 实现 1 磅/英寸 (4.4 N/25.4 mm) 热封强度的温度。 热封强度,Topwave HT 测试仪 0.5 S 保压,40 psi 压力,拉动速度 10(英寸/分)。 |
4 热封强度,Topwave HT 测试仪 0.5 S 保压,40 psi 压力,拉动速度 10(英寸/分)。 |
【新闻资讯】查看全部
“限塑令”推进,可降解材料“加速”替代
2022-08-24 扫描上图二维码,可以免费下载 搜料 APP 8月16日, 2022年全国塑料污染控制视频电话会议召开,由 国家发改委和生态环境部等21个塑料污染治理专项工作机制成员部门和单位联合进行。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |