| 牌号简介 About |
|---|
| 任务18是一种相对低粘度的铝填充聚氨酯铸造树脂，专门为制造短期真空成型模具而开发。当A和B部分按适当比例混合时，任务18在室温下固化过夜，收缩率可忽略不计，形成具有很高压缩和弯曲强度的非常硬的塑料。固化任务18可抛光、机加工、钻孔、喷漆等。任务18还可用于制造工业生产零件、原型零件和跟踪图案。（原名C-1508） TASK® 18 is a relatively low viscosity aluminum filled urethane casting resin that was developed specifically for making short run vacuum forming molds. When Parts A and B are mixed in proper proportion, TASK® 18 cures overnight at room temperature with negligible shrinkage to a very hard plastic that has a very high compressive and flexural strength. Cured TASK® 18 can be polished, machined, drilled, painted, etc. TASK® 18 is also used to make industrial production parts, prototype parts and tracing patterns. |
产品描述 Product Description
用途：成型;模板;
颜色：锡色
加工条件：浇铸 casting
性能特点： 可表面喷涂; 抗压性能好; 低粘度; 收缩性低; 可分散; Low Viscosity,Sprayable,Low contractility,Machinable,Good compressive strength
填料：金属填料
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.57 | g/cm³ | ASTM D1475 |
|
特定体积 Specific volume |
0.636 | cm³/g | ASTM D1475 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.060 | % | ASTM D2566 |
|
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脱模时间 stripping time 2 |
|||
|
23℃ 23℃ 2 |
960 | min | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
混合比 Mixing ratio |
26A:100B by weight | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ASTM D2240 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
压缩模量 Compression modulus |
MPa | ASTM D695 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
储存稳定性 storage stability |
|||
|
23℃ 23℃ |
min | ASTM D2471 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Cure Time |
|
【新闻资讯】查看全部
可互相衔接作为装饰品的塑料餐具
2016-01-22 来自德国汉诺威的ding3000工作室设计了这款命名为JOIN的塑料餐具，包括了刀、叉、勺，它们的特别之处是在手柄间都有一个卡口,通过卡口它们可以相互交织连接，因此，在其做完本职工作“餐具”被使用后，它们还搞点副业：业余兼职形成一个牢固的小型雕塑，装点餐桌，有各种颜色可供选择。 JOIN餐具设计还获得了“欧洲设计大奖”和“室内创新奖”的青睐。 来源： |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |