牌号简介 About |
---|
超高分子量聚乙烯薄膜(UHMW)具有极高的耐磨性,超过了钢的耐磨性。这种结合了广泛的化学阻力和低摩擦系数,使超高分子量微波成为一种非常多用途的工程材料,适用于许多苛刻的应用场合。应用实例包括饮用水的内表面和外表面、化学品、燃油和液压软管、滑雪板和滑雪板的底面以及减少摩擦和磨损的滑槽衬里。汽车挡风雨条。 Skived Ultra High Molecular Weight Polyethylene film (UHMW) UHMW has extremely high abrasion resistance, exceeding the abrasion resistance of steel. This coupled with broad chemcial resistance and low coefficient of friction makes UHMW an extremely versatile engineering material for many severe service applications. Application examples include inner and outer surfaces for potable water, chemical, fule and hydraulic hoses, bottom surfaces for skis and snow boards as well as linings for chutes to decrease friction and wear. Automotive weather stripping. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | |
吸水率 Water absorption rate |
|||
饱和 saturated |
0.010 | % | |
Thickness Thickness |
0.0762 到 2.36 | mm | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
MD,屈服 MD, yield |
41.4 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
MD,断裂 MD, fracture |
300 | % | ASTM D882 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ASTM C177 | |
变形 deformation 2 |
|||
50℃ 50℃ 2 |
% | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant 3 |
|||
1 MHz 1 MHz 3 |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Core ID Core ID |
cm | ||
Maximum Roll OD Maximum Roll OD |
mm | ||
Width Width 4 |
mm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2000 psi, 6 hr |
3 2H |
4 (increments of 1/16") |
【新闻资讯】查看全部
本周市场原油向好,需求预期持续恢复
2019-02-26 2019年春节后,国内聚乙烯行情快速下滑,元宵节后随着下游陆续恢复,市场止跌回稳,并小幅拉升,成交局面好转。本周市场原油向好,需求预期继续恢复,两大利好利多聚乙烯市场,预计下行受阻,可能小幅攀升。 从技术 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |