牌号简介 About |
---|
Sarlink TPV 4100系列是专为要求苛刻的汽车和工业应用而设计的工程材料。sarlink 4155是一种低密度、中等硬度的热塑性硫化胶,具有良好的压缩永久变形、弯曲疲劳、高温和低温性能。该材料可通过注射成型、吹塑和挤压加工,适用于密封件、垫圈、耐化学腐蚀软管和管道、靴子和波纹管等应用。 SARLINK® TPV 4100 series are engineered materials designed primarily for demanding automotive and industrial applications. Available in both black and natural, SARLINK® 4155 is a low density, medium hardness thermoplastic vulcanizate that exhibits excellent compression set, flex fatigue, high and low temperature performance. The material can be processed by injection molding, blow molding and extrusion for applications such as seals, gaskets, chemical resistant hose and tube, boots and bellows. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.958 | g/cm³ | ASTM D792 |
密度 Density |
0.960 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,100% 应变 TD, 100% strain |
2.00 | MPa | ASTM D412 |
TD,100% 应变 TD, 100% strain |
2.00 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
3.10 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D412 | |
断裂 fracture |
MPa | ISO 37 | |
MD,断裂 MD, fracture |
MPa | ISO 37 | |
MD,断裂 MD, fracture |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
断裂 fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
TD TD |
kN/m | ASTM D624 | |
TD TD 2 |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
|||
23℃,22 hr 23℃,22 hr |
% | ASTM D395 | |
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
ASTM D2240 | ||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
ISO 868 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ASTM D2240 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ISO 868 | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 - TD Change rate of tensile strength in air - TD |
|||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
100% 应变 135℃,1000 hr 100% strain 135 ℃, 1000 hr |
% | ASTM D573 | |
100% 应变 135℃,1000 hr 100% strain 135 ℃, 1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
100% 应变 150℃,168 hr 100% strain 150 ℃, 168 hr |
% | ASTM D573 | |
100% 应变 150℃,168 hr 100% strain 150 ℃, 168 hr |
% | ISO 188 | |
在空气中断裂时拉伸应力变化 - TD Changes in tensile stress when fractured in air - TD |
|||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
邵氏 A,135℃,1000 hr Shaw A, 135 ℃, 1000 hr |
ASTM D573 | ||
邵氏 A,135℃,1000 hr Shaw A, 135 ℃, 1000 hr |
ISO 188 | ||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ASTM D573 | ||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ISO 188 | ||
体积变化 Volume change |
|||
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ISO 1817 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.60 mm,黑色 0.60 mm, black |
UL 94 | ||
1.50 mm,本色 1.50 mm, natural color |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体表观粘度 - Capillary,@ 206/s Apparent viscosity of melt - Capillary, @ 206/s |
|||
200℃ 200℃ |
Pa·s | ASTM D3835 | |
200℃ 200℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 B 方法,直角形试样(不割口) |
【新闻资讯】查看全部
创维汽车计划明年上市 新手扎堆儿 跨界造车赛道疯狂
2021-04-30 搜料网资讯: 继百度、华为、恒大、小米、滴滴等企业下场造车后,家电行业巨头也开始入局。 4月27日,开沃新能源汽车集团在北京正式发布创维汽车品牌,汽车行业又迎来一名跨界新 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |