Cariflex® IR0310 K7U聚合物是一种高顺式-1,4含量的溶液聚合聚异戊二烯。它的对数固有粘度(liv)值为7.05 dl/g,具有高分子量。它由北美供应,物理形式如下所示。Cariflex® IR0310 K7U-作为白色/透明固体捆提供,以0.15%的典型值添加无污染稳定剂。Cariflex® IR0310 K7U聚合物按照最高标准制造,但特殊要求适用于某些敏感应用,如食品接触和药品。应始终参考规范这些应用的地方立法。Cariflex® IR0310 K7U聚合物在各种化合物中用作天然橡胶的替代品,具有颜色浅、均匀和杂质含量低的优点。其良好的流动特性改善了混合和成型性能。它用于食品和医药包装和密封,婴儿奶瓶和保健,粘合剂,橡胶的化学衍生物和非常浅色或透明的物品。 Cariflex IR0310 KU polymer is a solution polymerised polyisoprene with a high cis-1,4 content. It has a high molecular weight as indicated by its Logarithmic Inherent Viscosity (LIV) value of 7.05 dl/g. It is supplied from North America in the physical form identified below. Cariflex IR0310 KU - supplied as a white/transparent solid bale A non-staining stabilizer is added at the typical value of 0.15%. Cariflex IR0310 KU polymer is manufactured to the highest standards but special requirements apply to certain sensitive applications such as food contact and pharmaceuticals. Reference should always be made to local legislation regulating these applications. Cariflex IR0310 KU Polymer is used as a replacement for natural rubber in a wide range of compounds, offering advantages of light color, uniformity and low levels of impurities. Its good flow characteristics produce improvements in mixing and molding behavior. It is used for food and pharmaceutical packaging and seals, baby bottle teats and health care, adhesives, chemical derivatives of rubbers and very light colored or transparent articles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
门尼粘度 Mooney viscosity |
40 到 53 | MU | ASTM D1646 |
1,4顺式含量 1,4 cis content |
内部方法 | ||
-- -- 2 |
> 82.0 | wt% | 内部方法 |
-- -- 3 |
> 90.0 | wt% | 内部方法 |
Limiting Viscosity Number Limiting Viscosity Number |
700 到 1050 | cm³/g | 内部方法 |
Stabilizer Stabilizer |
0.10 到 0.30 | % | 内部方法 |
灰份含量 Ash Content |
% | 内部方法 | |
挥发物 Volatiles |
% | 内部方法 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 4 |
|||
流量,屈服 Flow rate, yield 4 |
MPa | ISO 37 | |
300% 应变 300% strain 4 |
MPa | ISO 37 | |
拉伸应变 Tensile strain 4 |
|||
断裂 fracture 4 |
% | ISO 37 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 NMR |
3 FTIR |
4 Cure: 40 min at 135°C |
【新闻资讯】查看全部
朗盛被CDP认定为全球气候保护领导者
2020-12-16 搜料网资讯: 朗盛在应对气候变化方面的努力再次得到了国际气候保护组织CDP的认可。在最近的一次评估中,这家特种化学品公司再次被列入气候A名单,成为该名单中全球270家公司之一 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |