| 牌号简介 About |
|---|
| 警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。-根据RTP公司提供的初步产品数据-根据RTP测试标准测试了列为可燃性（UL 94）的值。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- The value listed as Flammability, UL 94, was tested in accordance with RTP test standards. |
产品描述 Product Description
用途：齿轮;凸轮;
颜色：黑色,自然色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-0; 自润滑; 耐磨; 尺寸稳定性好; 润滑性; Good Dimensional Stability,Self-lubricating,Lubricating,Good wear resistance,V-0
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.61 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.10 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
0.060 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
3.2mm 3.2mm |
96 | J/m | ASTM D256 |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
3.2 mm 3.2 mm |
430 | J/m | ASTM D4812 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ASTM D696 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
|||
|
3.18 mm 3.18 mm |
sec | ASTM D495 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
3.20 mm 3.20 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
屈服 yield |
MPa | ASTM D638 | |
|
-- -- |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
ASTM D790 | ||
|
-- -- |
MPa | ASTM D790 | |
|
屈服 yield |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
摩擦系数 friction coefficient |
|||
|
与金属 - 动态 &Metal - Dynamic |
ASTM D1894 | ||
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部
上海石化塑料新品产量刷新纪录
2018-01-29 2017年，受市场、原料等因素影响，上海石化塑料部多套装置实施了经营性限产、停产。然而，就是在这样的严峻局面下，该公司塑料新产品却“逆势而上”，实现年度生产计划的114.49%。 长期以来，上海石化塑料部始终坚持差异化、高附加值的产品定位策略，不断开拓塑料产品新蓝海。 2017年，该公司塑料部将“己烯共聚工业化生产，改善管道料产品性能”作为新产品开发的重点，全年完成两次工业化试生产，并在收集用户质量反馈的基础上，不断调整工艺参数，力求产品力学性能达到试验要求 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付