牌号简介 About |
---|
Vydyne® 41 NT是一种通用的冲击改性PA66树脂。在自然条件下,由于PA66固有的所有加工和性能优势,加上改进的冲击强度,它被公认。该树脂具有高熔点、良好的表面润滑性、耐磨性和对许多化学品、机器和汽车油、溶剂和汽油的抵抗力等工程性能的良好平衡组合。Vydyne® 41 NT的设计是为了满足许多汽车技术规格中提出的关键低温冲击要求。 Vydyne 41 NT is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Vydyne 41 NT is designed to meet the critical low-temperature impact requirements called out in many automotive specifications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:2.0 mm TD:2.0 mm |
1.6 | % | ISO 294-4 |
MD:2.0 mm MD:2.0 mm |
1.8 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
2.1 | % | ISO 62 |
23℃,24hr 23℃,24hr |
1.0 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-40℃ -40℃ |
kJ/m² | ISO 179 | |
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
ISO 179 | ||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
-40℃ -40℃ |
kJ/m² | ISO 180 | |
-30℃ -30℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃,2 mm TD:23~55℃,2 mm |
1/℃ | ISO 11359-2 | |
MD:23~55℃,2 mm MD:23~55℃,2 mm |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
0.75 mm 0.75 mm |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
1 mm 1 mm |
kV/mm | IEC 60243 | |
耐电弧性 Arc resistance |
|||
3.0 mm 3.0 mm |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
3.00 mm 3.00 mm |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
汽车材料 Automotive materials |
|||
thickness d = 1 mm thickness d = 1 mm |
FMVSS 302 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
随着疫情限制措施的放松,废塑料热解项目重新启动
2021-07-12 搜料网资讯: Clean Vision Corporation的子公司Clean-Seas与总部位于伦敦的Roselle Capital宣布,双方已达成协议,成立一家合资企业,双方将合作在亚洲部署Clean-Seas公司的热解技术,将废弃塑料 |
随着疫情限制措施的放松,废塑料热解项目重新启动 搜料网资讯:Clean Vision Corporation的子公司Clean-Seas与总部位于伦敦的Roselle Capital宣布,双方已达成协议,成立一家合资企业,双方将合作在亚洲部署Clean-Seas公司的热解技术,将废弃塑料转化为有价值的商品或清洁能源。 作为一家独立的私募股权公司,Roselle Capital正积极开发Sabah Wellness Place医疗设施,该项目跨越三个地区,包括马来西亚、高加索国家格鲁吉亚和阿联酋。这些设施正在按照零排放的概念设计,包括绿色能源和塑料废物增值转化。 根据最终合资协议的条款,Roselle已要求Clean-Seas制定提案,在马来西亚和格鲁吉亚实施热解技术,以便安装在沙巴Wellness Place诊所以及这些国家的其他地方。 2020年,Clean-Seas公司已向马来西亚国家政府提交了一份初步提案,随后由于疫情的限制而被搁置。 该公司现已更新并重新向格鲁吉亚政府提交了该提案和一份类似提案。如果提案被接受,Roselle将为项目提供融资,双方将平等分享项目利润。 Clean Vision首席执行官Dan Bates表示:“长期以来,我们一直致力于通过我们的工业规模热解技术工厂,将废旧塑料转化为有价值的商品或绿色能源,并计划打入预计价值70亿美元的亚洲市场。” “随着全球商业和旅游业的重新开放,以及Roselle对融资及帮助我们在亚洲的计划取得成果的热情高涨,2021年将很快成为一个突破性的一年。此外,”Bates说,“我们在新英格兰的清洁海洋新商业计划正在继续获得各界的关注。” 亚洲废塑料热解市场机遇既适时又巨大。亚洲正在努力全面禁止在生态敏感或生态脆弱地区,包括靠近海洋、河流、湖泊、湿地的旅游区或其他水体和山脉中,非法处置塑料,以保护沿海、海洋和山区的生态系统和资源,同时牢记影响生态系统的广泛塑料垃圾。 此外,正如Roselle Capital高级负责人Shaun Wootton所指出的,对于格鲁吉亚和马来西亚等国而言,环境在其不断增长的生态旅游和其他旅游业中起着重要作用。 他补充说:“像马来西亚和格鲁吉亚这样的国家对这个问题相当敏感,建立将废弃塑料转化为商品或能源的工厂的能力——坚实的投资回报率和较短的投资回收期——使与Clean-Seas公司的合作成为一个双赢的提议。” 麦肯锡公司的一份报告支持这一观点。这份报告称,“塑料再利用和回收可为全球石油化工和塑料行业带来高达600亿美元的利润池增长,是目前的四倍。”在这一全球市场中,热解是最大的加工环节,占25.4%,是排名第二的单体回收的两倍以上。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。