| 概述：FZ-2130是一种30%玻璃纤维增强的线性聚苯硫醚化合物，具有良好的平衡性、优异的机械性能和加工性能。颜色：布莱克 Outline: FZ-2130 is a 30% glass fiber reinforced linear polyphenylene sulfide compound that is well balanced with excellent mechanical properties and processability. Color: Black |
产品描述 Product Description
颜色：黑色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-0; 易加工; Excellent Processability,V-0
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.56 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage rate |
ASTM D955 | ||
|
MD MD |
0.27 | % | ASTM D955 |
|
TD TD |
1.2 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
0.020 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
90 | J/m | ASTM D256 |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM D696 | ||
|
MD：-30~90℃ MD：-30~90℃ |
1/℃ | ASTM D696 | |
|
TD：-30~90℃ TD：-30~90℃ |
1/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
1.6 mm 1.6 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
0.80 mm 0.80 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
泊松比 Poisson's ratio |
|||
|
摩擦系数 friction coefficient 3 |
ASTM D1894 | ||
|
与钢 - 动态 Steel - Dynamic |
ASTM D1894 | ||
|
与钢 - 静态 Steel - Static |
ASTM D1894 | ||
|
断裂弯曲伸长率 Elongation at break and bending |
% | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 P=150KPa, V=0.3m/s |
|
【新闻资讯】查看全部
东芝扩建印度注塑机工厂
2016-01-05 日本东芝机械有限公司计划扩大其印度子公司的产能和产品范围，将生产1000吨以上的大型注塑机。 该公司将把钦奈工厂的产能从每年800台注塑机扩大到1000台以上，该公司告诉《塑料新闻》。 公司高管Girish Handigol表示，扩建将在未来三年内进行，已经购置了目前工厂隔壁的土地，以供扩建之需。 该公司还计划生产节能型和经济性系列，包括辅助系统。 该公司表示其印度业务的年增长率高达15%，高于10%的行业平均水平。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付