EMERGE™ PC/ABS 7590 高性能树脂是一种阻燃的PC/ABS共混物,不含氯、溴类添加剂。其优异的加工性能使其特别适宜于大型部件的模塑,可以在注塑加工过程中优化成型周期,提高生产效率。其 UL 94阻燃等级为V-0, 1.5mm。该树脂可广泛应用于信息技术设备和消费类电子设备 (ITE/CE)领域。 主要特性: UL 94阻燃等级为V-0, 1.5mm 不含氯、溴添加剂 应用领域: 电视机、显示器和PC外壳 稳压器和充电器。 EMERGE™ PC/ABS 7590 advanced resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. Its superior processing makes it ideal for molding large parts and optimizing cycle time productivity in injection molding operations. It has a UL 94 flammability rating of V-0 a 1.5mm. This resin is suitable for use in a wide variety of applications in the information technology equipment and consumer electronics (ITE/CE) markets. Main Characteristics: UL 94 V-0 at 1.5 mm Does not contain chlorine or bromine additives Applications: TV, monitor and PC enclosures Adaptors and chargers |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.17 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
230℃,3.80kg 230℃,3.80kg |
17 | g/10min | ASTM D1238 |
260℃,5.0kg 260℃,5.0kg |
75 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 to 0.60 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
46.2 | MPa | ASTM D638 |
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ASTM D638 | |
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 3 |
|||
1.50 mm 1.50 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index 3 |
% | ASTM D2863 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 标准 B (120°C/h), 压 力1 (10N) |
3 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
中化国际收购富比亚,进军塑料添加剂业务
2021-08-30 搜料网资讯: 中化国际宣布,公司已于8月26日完成对江苏富比亚化学品有限公司(以下简称富比亚)的收购,正式进军塑料添加剂业务。 江苏富比亚化学品有限公司 中化国际总经理刘 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |