牌号简介 About |
---|
ISPLEN® PR 240 G1F是一种中等熔融流速的丙烯-乙烯无规共聚物,具有基本配方,适于挤出。其配方中不含任何抗静电剂或成核添加剂。在挤出过程中,使用合适的颜料可以很容易地着色,最好是以浓缩物的形式,其熔体流动速率比碱聚合物的高。典型应用板材和热成型。瓦楞纸板。无取向薄膜、铸膜柔性管建议的熔化温度范围为190-250°C。应优化每条生产线的加工条件。 ISPLEN® PR 240 G1F is a medium melt flow rate propylene-ethylene random copolymer, with a basic formulation, adapted for extrusion. It does not include any antistatic agent or nucleating additives in its formulation. It can be easily coloured during the extrusion process using the right pigments, preferably in the form of concentrates with a higher melt flow rate than that of the base polymer. TYPICAL APPLICATIONS Sheets and thermoforming. Corrugated cardboard. Non-oriented film, Cast-film Flexible Pipes Recommended melt temperature range from 190 - 250°C. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
3.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
850 | MPa | ISO 178 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
9.0 | kJ/m² | ISO 179 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
75.0 | ℃ | ISO 75-2/B |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
宇航员尿液可回收制成养分品和3D打印塑料原料
2017-08-24 据英国《每日电讯报》网站22日报道,美国科学家已经证明,他们能利用酵母菌株,将宇航员们呼出的气体、排出的尿液等废物中的重要分子回收利用,再让其“变身”为营养品,或者3D打印原料,打印出塑料制品。 一般而言,宇航员不可能携带很多零件和物品前往太空,因为负载越多,逃离地球引力前往太空的成本越高。现在,在美国国家航空航天局(NASA)的资助下,美国克莱姆森大学的研究人员发现,不同的酵母菌株能将人类排出的废物变成有用的物品。 例如,一种酵母菌株,在被喂食了未被处理的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |