| 牌号简介 About |
|---|
| Torlon 4630是可注射成形的耐磨级聚酰胺酰亚胺（PAI）树脂，主要为非润滑产品提供卓越的抗磨抗性能。在275 ℃（ 525°F ）环境下，Torlon PAI所具有的强度和刚度超过所有热塑性塑料 ，并具有优异的耐磨损性、抗蠕变和化学品。 Torlon 4630聚酰胺 - 酰亚胺的潜在应用包括止推垫圈、密封圈、滑动叶片、线轴、衬套、离合器辊和活塞。 Torlon® 4630 is an injection-moldable, wear-resistant grade of polyamide-imide (PAI), that has been formulated to give outstanding wear resistantance in non-lubricated applications. Torlon® PAI has the highest strength and stiffness of any thermoplastic up to 275°C (525°F). It has outstanding resistance to wear, creep and chemicals. Potential applications for Torlon® 4630 polyamide-imide include thrust washers, seal rings, sliding vanes, bobbins, bushings, clutch rollers and pistons. |
产品描述 Product Description
用途：轴承;汽车领域的应用;衬套;
加工条件：型材挤出成型 Profile extrusion
性能特点： 耐磨; 机械强度好; 耐化学性; 耐高温; 阻燃; 低摩擦系数; 韧性好; Good Rigidity,Good flexibility,Low coefficient of friction,Flame Characteristics,High Heat Resistance,Good wear resistance,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.56 | g/cm³ | ASTM D792 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
0.18 | % | ASTM D570 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
7450 | MPa | ASTM D638 |
|
拉伸强度 tensile strength |
81.4 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
1.9 | % | ASTM D638 |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
摩擦系数 friction coefficient |
|||
|
-- -- 2 |
ASTM D3702 | ||
|
-- -- 3 |
ASTM D3702 | ||
|
-- -- 4 |
ASTM D1894 | ||
|
-- -- 5 |
ASTM D1894 | ||
|
磨损因数 Wear factor |
ASTM D3702 | ||
|
干燥： 4 m/s，0.2 MPa（800 fpm，31.25 psi） Drying: 4 m/s, 0.2 MPa (800 fpm, 31.25 psi) |
in³·min^-10/ft·lb·hr | ASTM D3702 | |
|
干燥：0.25 m/s，3.4 MPa（50 fpm，500 psi） Drying: 0.25 m/s, 3.4 MPa (50 fpm, 500 psi) |
in³·min^-10/ft·lb·hr | ASTM D3702 | |
|
润滑： 4 m/s，5.2 MPa（800 fpm，750 psi） Lubrication: 4 m/s, 5.2 MPa (800 fpm, 750 psi) |
in³·min^-10/ft·lb·hr | ASTM D3702 | |
|
润滑：0.375 m/s，6.9 MPa（75 fpm，1000 psi） Lubrication: 0.375 m/s, 6.9 MPa (75 fpm, 1000 psi) |
in³·min^-10/ft·lb·hr | ASTM D3702 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
cm/cm/℃ | ASTM D696 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 润滑： 0.25 m/s, 6.9 MPa (75 fpm, 1000 psi) |
| 3 润滑： 4 m/s, 5.2 MPa (800 fpm, 750 psi) |
| 4 干燥：0.25 m/s, 3.4 MPa (50 fpm, 500 psi) |
| 5 干燥： 4 m/s, 0.2 MPa (800 fpm, 31.25 psi) |
|
【新闻资讯】查看全部 
美丽中国拟涉足废塑料高温分解业务
2021-05-16 搜料网资讯： 美丽中国控股(00706-HK)公告，公司及山东开元就建议注资订立谅解备忘录，谅解备忘录主要条款为集团建议以向山东开元之注册资本以注资方式，投资于山东开元，注资金额 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付