| 牌号简介 About |
|---|
| Westlake ELEVATE™ EM518AA是一种乙烯-醋酸乙烯共聚物，18.5%VA。EM518AA设计用于注塑、复合、发泡和一般挤出等应用。该材料具有优异的低温脆性、熔融强度和柔韧性。应用/用途：注射成型复合泡沫 Westlake ELEVATE™ EM518AA is an ethylene vinyl acetate copolymer with 18.5% VA. EM518AA is designed for use in applications such as injection molding, compounding, foaming, and general extrusion. This material has excellent low temperature brittleness properties, melt strength, and flexibility. Application/Uses: Injection Molding Compounding Foam |
产品描述 Product Description
用途：泡沫;复合;
加工条件：复合
性能特点： 熔体强度好; 共聚物; 耐低温; 韧性好; Good flexibility,Antifreeze,Good melt strength,Copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.940 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
2.5 | g/10min | ASTM D1238 |
|
醋酸乙烯含量 Vinyl acetate content |
18.5 | wt% | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，15 秒，模压成型 Shore D, 15 seconds, molded |
32 | ASTM D2240 | |
|
拉伸强度 tensile strength |
|||
|
断裂，模压成型 Fracture, molded |
12.0 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain |
|||
|
断裂，模压成型 Fracture, molded |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
1% 正割，模压成型 1% cut, molded |
MPa | ASTM D790 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
熔融峰值温度 Melting peak temperature |
℃ | Internal Method | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
100%生物基材料PEF介绍！比PET更优秀的低碳材料！
2023-09-13 扫描上图二维码，可以免费下载 搜料 APP PEF，中文名为聚2,5-呋喃二甲酸乙二醇酯，英文名为Polyethylene2,5-furandicarboxylate，是一种100%生物基聚酯，以FDCA为单体，加入乙二醇通过直接酯化法 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |