牌号简介 About |
---|
INFUSE™ 9500烯烃嵌段共聚物是一种烯烃共聚物,具有优异的流动特性,在广泛的通用热塑性弹性体应用中表现良好,如注塑和型材挤出。INFUSE™ 9500在聚丙烯(PP)和聚乙烯(PE)的二次成型应用中提供出色的触觉。此外,其高结晶温度和低密度通过减少循环时间和减少零件重量来降低生产成本。主要特点:高工作温度性能、高弹性、良好的弹性恢复、加工性快速设置时间、通用弹性体、适用于化合物和混合物,符合:欧盟,2011年10月,美国食品和药物管理局FCN 424。有关完整的详细信息,请参考法规。 INFUSE™ 9500 Olefin Block Copolymer is a olefin copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications, such as injection molding and profile extrusion. INFUSE 9500 provides outstanding haptics in over molding applications with polypropylene (PP) and Polyethylene (PE). In addition, its high crystallization temperature and lower density drive lower production costs by reducing cycle time and reducing part weight. Main Characteristics: High upper service temperature performance Highly flexible with good elastic recovery Fast set up times for processability General purpose elastomer Excellent for compounds and blends Complies with: EU, No 10/2011 U.S. FDA FCN 424 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.877 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
5.0 | g/10min | ASTM D1238 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
4.98 | MPa | ASTM D638 |
断裂 fracture |
9.50 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
1200 | % | ASTM D638 |
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395 | ||
21℃ 21℃ |
% | ASTM D395 | |
70℃ 70℃ 2 |
% | ASTM D395 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
TMA(2.54 cm) TMA(2.54 cm) 3 |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,模压成型 Shaw A, molded |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
|||
100% 正割,模压成型 100% cut, molded |
MPa | ASTM D638 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 5°C/分 |
3 1N,5°C/分 |
【新闻资讯】查看全部
克劳斯玛菲新建汉诺威工厂 集中整合挤出类业务
2021-05-18 搜料网资讯: 通过集中所有的挤出业务,克劳斯玛菲集团已将其在挤出领域的技术专知和数十年的经验捆绑在一起。这种战略方式,将为客户带来实质性的产品利益,为公司带来价值协 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |