牌号简介 About |
---|
Hyflon PFA是一个独特的半结晶、可熔融处理的全氟聚合物家族,它结合了优异的机械特性和独特的性能,如化学惰性、耐热性、固有的阻燃性、低表面能和特殊的介电性能。Hyflon PFA树脂设计用于在低温到250-260°C(482-500°F)的各种温度范围内保持其性能,是化学加工工业、石油和天然气、特种电缆、半导体工业、航空航天和其他具有挑战性的行业中衬里等应用的首选材料。Hyflon® PFA 125X是一种非常低的熔融流动速率树脂,设计用于管道挤压,在那里需要非常高的粘度和熔融强度。与标准PFA相比,它对气体的渗透性也显著降低。Hyflon PFA P125X是一种ASTM D3307型XV树脂。 Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resistance, inherent flame resistance, low surface energy, and exceptional dielectric properties. Hyflon® PFA resins have been designed to retain their properties over a wide range of temperatures from cryogenic to 300°C (572°F) and are the material of choice in applications such as linings in the Chemical Process Industry, Oil and Gas, Specialty Cables, Semiconductor Industry, Aerospace, and other challenging industries. Hyflon® PFA 125X is a low melt flow rate resin designed for pipe extrusion, where very high viscosity and melt strength are needed. It also has significantly lower permeability to gasses than standard PFAs. Hyflon® PFA P125X is an ASTM D3307 - Type XV resin. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
372℃,5.0kg 372℃,5.0kg |
1.5 到 3.0 | g/10min | ASTM D1238 |
1%重量损失(TGA) 1% weight loss (TGA) |
1.2E-4 到 2.0E-4 | cm/cm/℃ | ASTM D696 |
密度 Density |
2.120 到 2.170 | g/cm³ | ASTM D792 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
no break | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
310 到 316 | ℃ | ASTM D4591 |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | ASTM D4591 | |
导热系数 Thermal conductivity coefficient |
|||
40℃ 40℃ |
W/m/K | ASTM C177 | |
结晶热 Crystallization heat |
J/g | ASTM D4591 | |
融合热量 Fusion heat |
J/g | ASTM D4591 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus 2 |
|||
280℃ 280℃ 3 |
MPa | ASTM D1708 | |
23℃ 23℃ 2 |
MPa | ASTM D1708 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D1708 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D1708 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.039 in/min |
3 1mm/min |
【新闻资讯】查看全部
中国石油自主研发茂金属聚丙烯催化剂工业试验成功
2020-11-19 搜料网资讯: 近日,中国石油石油化工研究院自主研发的茂金属聚丙烯催化剂MPP-S02,在山东一大型化工公司进行工业试验,获得圆满成功,顺利开发出两种茂金属超高熔体质量流动速率 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |