牌号简介 About |
---|
非常高的抗环境应力开裂(VH ESCR)HIPS。ICE S 900具有高韧性,对油、脂肪和化学试剂,特别是环戊烷具有优异的耐化学性。适用于挤出/热成型和注塑成型。名称:热塑性塑料ISO 2897-PS-I,G,093-03-07-12应用,设计用于冰箱内衬和框架,其中环戊烷用作绝缘聚氨酯泡沫的发泡剂。ICE S 900显著改善了热成型过程中的壁厚分布,并允许优化原始挤压板的厚度。 Very high environmental stress cracking resistant (VH ESCR) HIPS. ICE S 900 exhibits high toughness and excellent chemical resistance to oils, fats and chemical agents and in particular to cyclopentane. Suitable for extrusion / thermoforming and injection moulding. Designation: Thermoplastics ISO 2897-PS-I,G,093-03-07-12 Applications Designed for inner liners and frames for refrigerators where cyclopentane is used as blowing agent for insulating polyurethane foams. ICE S 900 significantly improves the wall thickness distribution in thermoforming and allows to optimize the thickness of the original extruded sheet. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.65 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
2.5 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.40 到 0.70 | % | 内部方法 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.10 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
ISO 527-2/50 | ||
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ISO 8302 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
50 Hz 50 Hz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
50 Hz 50 Hz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.5 mm,Internal testig 1.5 mm,Internal testig |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
印度疫情难阻OPEC+增产决心 “需求没问题”信号推动油价不跌反涨
2021-04-28 搜料网资讯: 尽管印度疫情部分打压了原油需求,但OPEC+依旧看好全球经济复苏下的需求前景,周二OPEC在官网发布声明,确认维持5-7月的增产计划。 尽管OPEC+决定增产,但背后透露的需 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |