| 牌号简介 About |
|---|
| 总聚丙烯3281的高熔融强度允许在加工过程中均匀拉伸，从而使生产线速度达到最大，物理性能达到良好的平衡。总聚丙烯3281具有优异的聚合物稳定性，即使使用再研磨剂，也能在挤出过程中产生一致的产品性能。总聚丙烯3281符合所有适用的FDA法规，可根据这些规定用于食品接触应用。对于要求高熔融强度和高挤出速度的片材和捆扎应用，建议使用总聚丙烯3281。 Polypropylene 3281: The high melt strength of TOTAL Polypropylene 3281 allows uniform draw down during processing, resulting in maximum line speeds and a good balance of physical properties. Process Stability: Excellent polymer stability of TOTAL 3281 produces consistent product properties during extrusion, even with the use of regrind. FDA: 3281 complies with all applicable FDA regulations and may be used under these provisions for food contact applications. Applications: 3281 is recommended for sheet and strapping applications where high melt strength and high extrusion speeds are required. Processing: 3281 resin processes on conventional extrusion equipment with typical melt temperatures of 390-450°F (200-232°C). |
产品描述 Product Description
用途：片材;皮带材料;热成型应用;
加工条件：片材挤出成型
性能特点： 熔体强度好; 流动性低; 均聚物; 食品接触; Low liquidity,Food contact compliance,Good melt strength,Homopolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.905 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
1.3 | g/10min | ASTM D1238 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
43 | J/m | ASTM D256-A |
|
23℃ 23℃ |
1600 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
104 | ℃ | ASTM D648 |
|
熔融温度 Melting temperature |
℃ | DSC | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ASTM D696 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ASTM D1706 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
零部件日趋大型直接导致模具必须大型化
2021-04-16 搜料网资讯： 近年来，随着我国行业结构调整步伐加快，模具越来越趋向大型化、精密化、复杂化方向发展，这是由于高生产效率要求而决定的。为了提高生产效率而发展起来的一模多 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付