| 牌号简介 About |
|---|
| AV-755 SL45是一种耐磨等级的芳基醚酮（PAEK），设计用于在润滑磨损环境中提供低磨损率和高压速度（PV）公差。与Avaspire AV-700系列的其他成员一样，AV-755SL45提供了比Peek更具吸引力的经济性，同时保留了Peek的大部分关键属性。除了优异的耐磨性外，该树脂还具有优异的耐化学性、高温下的机械强度和刚度以及长期和高温热氧化稳定性。AV-755 SL45是由碳纤维和石墨组成的二元抗摩擦/耐磨添加剂系统。由于其添加系统，这种树脂也提供，特别高的硬度和非常低的吸湿性。AV-755SL45的潜在应用包括衬套、轴承、耐磨条、耐磨环、滚子和滑动摩擦部件中使用的其他零件。这种高流动性（低粘度）树脂是黑色的。 AV-755 SL45 is a wear resistant grade of AvaSpire® polyaryletherketone (PAEK) designed to provide low wear rates and high pressure-velocity (PV) tolerance in lubricated wear environments. Like the other members of the AvaSpire® AV-700 series, AV-755 SL45 offers more attractive economics than PEEK while retaining most of PEEK's key attributes. In addition to the outstanding wear resistance, the resin also offers the outstanding combination of chemical resistance, mechanical strength and stiffness at elevated temperatures, as well as long-term and high temperature thermal-oxidative stability. AV-755 SL45 is formulated with a binary anti-friction/anti-wear additive system comprised of carbon fiber and graphite. By virtue of its additive system, this resin also offers, exceptionally high stiffness and very low moisture absorption. Potential applications for AV-755 SL45 include bushings, bearings, wear strips, wear rings, rollers, and other parts used in sliding friction components. This high flow (low viscosity) resin is black. |
产品描述 Product Description
用途：轴承;汽车领域的应用;密封件;衬套;止推垫圈;滚轴;防磨条;
颜色：黑色
加工条件：注射成型 Injection Molding
性能特点： 耐磨; 尺寸稳定性好; 耐化学性; 耐高温; 阻燃; Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Good wear resistance,Solvent resistance
填料：碳纤维
| 技术参数 Technical Data | |||
|---|---|---|---|
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
-- -- |
53 | J/m | ASTM D256 |
|
-- -- |
6.8 | kJ/m² | ISO 180 |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
-- -- |
320 | J/m | ASTM D4812 |
|
-- -- |
25 | kJ/m² | ISO 180 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 7 |
|||
|
1.8 MPa，退火，3.2 mm 1.8 MPa, annealed, 3.2 mm 7 |
278 | ℃ | ASTM D648 |
|
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-50~50℃ MD：-50~50℃ |
1/℃ | ASTM E831 | |
|
比热 specific heat |
DSC | ||
|
50℃ 50℃ |
J/kg/℃ | DSC | |
|
200℃ 200℃ |
J/kg/℃ | DSC | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
|||
|
-- -- 3 |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2/1A/5 | |
|
-- -- 3 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture 3 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
弯曲模量 Bending modulus |
|||
|
-- -- |
MPa | ASTM D790 | |
|
-- -- |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
-- -- |
MPa | ASTM D790 | |
|
-- -- |
MPa | ISO 178 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
MPa | ASTM D732 | |
|
摩擦系数 friction coefficient |
ASTM D3702 | ||
|
-- -- 4 |
ASTM D3702 | ||
|
-- -- 5 |
ASTM D3702 | ||
|
-- -- 6 |
ASTM D3702 | ||
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ASTM D792 | |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
400℃，2.16kg 400℃，2.16kg |
g/10min | ASTM D1238 | |
|
收缩率 Shrinkage rate 2 |
ASTM D955 | ||
|
MD：3.2 mm MD：3.2 mm |
% | ASTM D955 | |
|
TD：3.2 mm TD：3.2 mm |
% | ASTM D955 | |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
% | ASTM D570 | |
|
熔体表观粘度 Apparent viscosity of melt |
|||
|
400℃，1000 sec^-1 400℃，1000 sec^-1 |
Pa·s | ASTM D3835 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 5" x 0.5" x 0.125" bars |
| 3 0.20 in/min |
| 4 润滑条件： 800 fpm ， 750 psi (6.06 m/s ， 5171 kPa) |
| 5 润滑条件： 75 fpm， 1000 psi (0.38 m/s ， 6895 kPa) |
| 6 干燥条件： 800 fpm，31.25 psi (4.06 m/s，215 kPa)。不推荐 50 fpm，500 psi (0.25 m/s，3447 kPa)。 |
| 7 200°C，2小时 |
|
【新闻资讯】查看全部 
宁波北仑1天新增13例，已提级临时性全域静默管理！
2022-10-17 扫描上图二维码，可以免费下载 搜料 APP 中国第二大、全球第三大集装箱港宁波舟山港核心港区所在地--宁波北仑再次出现新冠确诊病例。 10月16日0-19时，宁波市北仑区新增12例确诊病例 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付