| 牌号简介 About |
|---|
| SABIC® LLDPE 726QJ是一种丁烯线性低密度聚乙烯树脂。这一等级通常被设计为使吹塑薄膜具有相对较高的刚度，从而具有良好的可加工性和其他性能（如耐穿刺性、冲击强度和热密封性）的良好总体平衡性。这种材料含有防堵、防滑剂和加工助剂。SABIC® LLDPE 726QJ的典型应用是运输袋、生产袋、罐衬和运输袋。SABIC® LLDPE 726QJ与低密度聚乙烯（15-85%）混合时具有良好的光学性能。本产品不适用于任何医药/医疗应用，也不得用于任何医药/医疗应用。 SABIC® LLDPE 726QJ is a butene linear low density polyethylene resin. This grade is typically designed to give blown films a relatively high stiffness for good machinability and a good overall balance of other performance properties, such as puncture resistance, impact strength and heat sealability. This material contains anti block, slip erucamide and processing aid. Application Typical applications for SABIC® LLDPE 726QJ are shipping sacks, produce bags, can liners and carrier bags. SABIC® LLDPE 726QJ has good optical properties when blended with a LDPE (15-85%). This product is not intended for and must not be used in any pharmaceutical/medical applications. |
产品描述 Product Description
用途：薄膜;衬里;袋子;吹膜;
加工条件：吹塑薄膜
性能特点： 抗结块性; 机械强度好; 抗氧化; 高光滑性; 丁烯共聚单体; 冲击性能好; 低密度; 线性高分子结构; 热封性好; 可分散; 抗穿孔性; Good Rigidity,Good heat sealing,High impact resistance,Smoothness,High anti-blocking,Machinable,Inoxidizability,Low density,Linear polymer structure,Butylene copolymer,Puncture Resistant
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.926 | g/cm³ | ISO 1183/A |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.70 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 friction coefficient |
|||
|
吹塑薄膜 Blown film |
0.10 | ISO 8295 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
50 | µm | |
|
拉伸模量 Tensile modulus |
ISO 527-3 | ||
|
MD，50 µm，吹塑薄膜 MD, 50 µ m, blow molded film |
220 | MPa | ISO 527-3 |
|
TD，50 µm，吹塑薄膜 TD, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，50 µm，吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，屈服，50 µm，吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁冲击强度 Izod notched impact strength |
|||
|
50µm,吹塑成型 50 µ m, blow molded |
J/cm | ASTM D4272 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，50.0 µm，吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻塞力 Blocking force |
|||
|
吹塑薄膜，50.0 µm Blow molded film, 50.0 µ m |
g | 内部方法 | |
|
抗穿刺性 Puncture resistance |
|||
|
吹塑薄膜，50.0 µm Blow molded film, 50.0 µ m |
J/m | 内部方法 | |
|
Re-blocking - 吹塑薄膜（50.0 µm） Re blocking - blow molded film (50.0 µ m) |
g | 内部方法 | |
|
撕裂强度 tear strength 2 |
ISO 6383-2 | ||
|
MD，50 µm MD，50 µm |
kN/m | ISO 6383-2 | |
|
TD，50 µm TD，50 µm |
kN/m | ISO 6383-2 | |
| 备注 |
|---|
| 2 Blown Film |
|
【新闻资讯】查看全部 
联合国秘书长呼吁对大型石油和天然气公司征税
2022-08-05 联合国秘书长古特雷斯3日呼吁各国政府对从当前能源危机中获得巨额利润的大型石油和天然气公司征税。 古特雷斯在联合国全球粮食、能源和金融危机应对小组第三份报告的记者招待 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付