牌号简介 About |
---|
Pro-fax RP320N裸脚聚丙烯无规共聚物以颗粒形式提供。该树脂通常用于铸膜应用,与均聚聚丙烯相比,具有优异的透明度和光泽度,以及更好的耐低温冲击性和更宽的热密封范围。有关法规遵从性信息,请参阅Pro-fax RP320N产品管理公告(PSB)。 Pro-fax RP320N barefoot polypropylene random copolymer is available in pellet form. This resin is typically used in cast film applications and offers exceptional clarity and gloss, as well as improved cold temperature impact resistance and broader heat seal range compared to homopolymer polypropylene. For regulatory compliance information see Pro-fax RP320N Product Stewardship Bulletin (PSB). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.9 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
12 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
81.1 | ℃ | ASTM D648 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
58.7 | J/m | ASTM D256 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
81 | R 级 | ASTM D785 |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.051 in/min |
【新闻资讯】查看全部
朗盛发行6亿欧元与其可持续发展目标挂钩的债券
2021-12-05 搜料网资讯: 朗盛 坚定了其在可持续金融领域的承诺,并成功将其首个可持续发展相关债券投放到欧洲资本市场。规模为6亿欧元的基准债券的期限为8年,票面利率为0.625%。债券的利率 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |