牌号简介 About |
---|
WC-783 A/B是一种抗冲击、刚性、82邵氏D材料,常用于制造各种透明或着色铸件。当在室温下使用时,厚度为1/8英寸或更大的铸件可轻易铸造。厚度小于1/8“的铸件通常需要轻微的后固化。 WC-783 A/B is an impact resistant, rigid, 82 Shore D material that is commonly used to make clear or tinted castings of all kinds. The standard work time is 15 minutes, however 6 additional work speeds are available. A mild post-cure is recommended for best results. Exceptional clarity No odor Impact resistant UV light and oxidation resistance Good exterior weatherability, light stable |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
53 | J/m | ASTM D256 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time 6 |
|||
25℃ 25℃ 6 |
5.0 到 7.0 | day | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
80 到 84 | ASTM D2240 | |
拉伸模量 Tensile modulus |
1790 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
屈服 yield |
45.9 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
密度 Density |
|||
Part A Part A |
g/cm³ | ||
Part B Part B |
g/cm³ | ||
收缩率 Shrinkage rate |
|||
-- -- 3 |
% | ||
布络克菲尔德粘度 Brookfield viscosity |
|||
混合,25℃ Mixing, 25 ℃ |
mPa·s | ||
Part A,25℃ Part A,25℃ |
mPa·s | ||
Part B,25℃ Part B,25℃ |
mPa·s | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
-20~130℃ -20~130℃ |
|||
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
wk | ||
脱模时间 stripping time |
|||
25℃ 25℃ |
hr | ||
工作时间 working hours 5 |
|||
25℃ 25℃ 5 |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 12"x1/2"x1/2", 5 min work time |
3 12"x1/2"x1/2", 15 min work time |
4 12"x1/2"x1/2", 30 min work time |
5 100g |
6 For maximum physical properties, a post cure with heat is required (16 hrs at 180°F). Cure will be inhibited if cast against a tin catalyzed silicone RTV. |
【新闻资讯】查看全部
中科院团队研发绿色低碳成套新技术实现十万吨级工业装置运行
2022-05-25 从中国科学院过程工程研究所(中科院过程工程所)获悉,该所研发的离子液体催化二氧化碳合成碳酸酯绿色低碳成套新技术近日通过中国石油和化学工业联合会组织的成果鉴定。这项成 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |