牌号简介 About |
---|
HBG5723FR为增强型PBT/ABS树脂。HBG5723FR具有优异的机械强度、高耐化学腐蚀性和高耐成型性能。HBG5723FR主要用于除草机、汽车零部件、电子电器零部件等。 HBG5723FR is reinforced PBT/ABS resin. HBG5723FR has excellent mechnical strength, high chem-resistance and high shape resistance property. HBG5723FR is mainly used in weeding machine, automobile parts, electric & electron parts, etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.32 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,5.0kg 250℃,5.0kg |
25 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.20 到 0.40 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
80.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
10 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
新型石墨烯氧化物薄膜可更好淡化海水
2017-04-06 英国曼彻斯特大学研究人员3日在《自然・纳米技术》发表报告说,他们开发的一种新型石墨烯氧化物薄膜能更高效地过滤海水中的盐,未来在海水淡化产业中有非常好的应用前景。 氧化石墨烯薄膜在气体分离和水处理方面已经展示了很大的应用潜力,但现有的这类薄膜还无法适应海水淡化工艺要求。曼彻斯特大学此前的研究就发现,如果将这类薄膜浸泡在水中,它会轻微膨胀,微小的盐离子会随着水流渗透薄膜,无法完成对盐的过滤。 为解决这个问题,研究团队利用环氧树脂涂层在薄膜两边形成“阻隔墙”,有效 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |