Shinil最近开发了各种热塑性塑料(主要是聚丙烯、尼龙和聚酯)的长玻璃纤维增强复合材料。本产品旨在提供优异的强度和韧性,以及优异的热稳定性和尺寸稳定性。Shinil的LFT化合物可以用来代替金属,特别是用来制作门饰板、模数、洗衣机浴缸、前端模块、风扇罩。 Shinil has recently developed long glass fiber reinforced compound with various thermoplastics, mainly PP, Nylon and Polyesters. This products are designed to offer excellent strength and toughness with excellent thermal and dimensional stability. Shinil's LFT compound can be used to replace metal specially to make door trim, modulus, washing machine tubs, front end module, fan shroud. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
0.20 到 0.60 | % | 内部方法 |
灰份含量 Ash Content |
38 到 42 | % | ISO 3451-1 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
11000 | MPa | ISO 527-2/5 |
拉伸强度 tensile strength |
|||
断裂 fracture |
120 | MPa | ISO 527-2/5 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
|||
DSC DSC 2 |
℃ | ISO 3146 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity 3 |
ohms | IEC 60093 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
3 23°C/50% RH |
【新闻资讯】查看全部
Sinterline® Technyl® 粉末助推Polimotor-2全…
2015-12-14 专为激光烧结工艺设计的Sinterline®技术可利用三维打印工艺制造发动机进气歧管,优异性能表现可与注塑成型件相媲美。 全球高端聚酰胺解决方案领导者索尔维工程塑料近日宣布,在全新的前瞻性汽车全塑发动机项目Polimotor-2中,将采用选择性激光烧结(SLS)工艺(一种三维打印技术)制造发动机的进气歧管部分。而在这一尖端技术的背后,索尔维提供的Sinterline® Technyl®聚酰胺6(PA6)粉末功不可没。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |