牌号简介 About |
---|
Ultramid® 2412GFH6 Bright是一种聚酰胺66,用33%的玻璃纤维增强,用于注塑成型。该等级在热性能和机械性能之间提供了极好的结合 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
成型收缩率 molding shrinkage Forming shrinkage |
|||
MD MD |
0.28 | % | ISO 294-4 |
TD TD |
0.98 | % | ISO 294-4 |
吸水率 water absorption Water absorption |
|||
24 h 在水中 in the water,23℃ 24 hours in the water at 23 ℃ |
0.9 | % | ISO 62 |
平衡 equilibrium,23℃ Equilibrium equilibrium, 23 ℃ |
5.5 | % | ISO 62 |
吸水率 moisture absorption Moisture absorption |
|||
平行,23℃,50%湿度 r.h. Parallel, 23 ℃, 50% humidity, r. h |
1.6 | % | ISO 62 |
密度 density Density |
|||
|
kg/m³ | ISO 1183 | |
ASTM ASTM |
g/cm³ | ASTM D792 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus Tensile modulus |
|||
干燥 dry Dry |
MPa | ISO 527-2 | |
湿润 cond Wet Cond |
MPa | ISO 527-2 | |
拉伸强度 Tensile strength Tensile strength |
|||
50 mm/min ,干燥 dry,屈服 yld 50 mm/min, dry, yield yld |
MPa | ISO 527-2 | |
2 in/min ,干燥 dry,屈服 yld 2 in/min, dry, yield yld |
MPa | ASTM D638 | |
干燥 dry,断裂 break Dry, broken |
MPa | ISO 527-2 | |
湿润 cond,断裂 break Wet cond, fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain Tensile strain |
|||
断裂 break,干燥 dry Break, dry dry |
% | ISO 527-2 | |
断裂 break,湿润 cond Break, wet cond |
% | ISO 527-2 | |
断裂伸长率 elongation at break Elongation at break |
|||
2 in/min,干燥 dry 2 in/min, dry |
% | ASTM D638 | |
弯曲模量 Flexural modulus |
|||
|
MPa | ISO 178 | |
ASTM ASTM |
MPa | ASTM D790 | |
弯曲强度 Flexural strength |
|||
|
MPa | ISO 178 | |
ASTM,干燥 dry ASTM, dry |
MPa | ASTM D790 | |
ASTM,湿润 cond ASTM, Wet Cond |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched impact strength Charpy notched impact strength |
|||
干燥 dry Dry |
kJ/m² | ISO 179/1eA | |
湿润 cond Wet Cond |
kJ/m² | ISO 179/1eA | |
简支梁冲击强度 Charpy impact strength Charpy impact strength of simply supported beams |
|||
干燥 dry Dry |
KJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Izod notched impact strength Izod notched impact strength |
|||
干燥 dry Dry |
KJ/m² | ISO 180/1A | |
湿润 cond Wet Cond |
J/m | ASTM D256 | |
干燥 dry Dry |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.80 MPa 1.80 MPa |
℃ | ISO 75-1/-2 | |
1.82 MPa 1.82 MPa |
℃ | ASTM D648 | |
熔融温度 melting temperature Melting temperature |
℃ | ISO 11357-3 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
|||
干燥 dry Dry |
ohm | IEC 62631-3-2 | |
湿润 cond Wet Cond |
ohm | IEC 62631-3-1 | |
体积电阻率 Volume resistivity |
|||
干燥 dry Dry |
ohm·m | IEC 60243-1 | |
湿润 cond Wet Cond |
ohm·m | IEC 60243-1 | |
介电强度 Electric strength Electric strength |
|||
d=2 mm,干燥 dry D=2 mm, dry |
kV/mm | IEC 62631-2-1 | |
d=2 mm,湿润 cond D=2 mm, moist cond |
kV/mm | IEC 62631-2-1 | |
耗散因数 Dissipation factor Dissipation factor |
|||
干燥 dry Dry |
E-4 | IEC 60112 | |
湿润 cond Wet Cond |
E-4 | IEC 60112 | |
相比漏电起痕指数 Comparative tracking index Compared tracking index |
|||
测试液A test liquid A,干燥 dry Test liquid A, dry |
IEC 60112 | ||
测试液A test liquid A,湿润 cond Test liquid A, wet cond |
IEC 60112 | ||
测试液B test liquid A,干燥 dry Test liquid A, dry |
IEC 60112 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
|||
0.8 mm 0.8 mm |
calss | IEC 60695-11-10 | |
灼热丝可燃性指数 Glow Wire Flammability Index Glow Wire Flammability Index |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Oxygen index Oxygen index |
% | ISO 4589-2 |
备注 |
---|
对于增强聚酰胺,BASF SE建议使用碳含量高的钢,并进行净化抛光,以避免或限制磨损。 建议使用加工温度等加工参数,可根据注塑机尺寸、零件几何形状/设计进行调整 |
【新闻资讯】查看全部 |
||
新型塑料给地球降温 便宜降温塑料 无需通电,无需烧电,自身就能降温;不把压力返给地球上一切其他物品,立即把不必要的发热量送至外太空;另外环保节能、低碳环保、高效率、翠绿色、环境保护……这款理想化的降温材料并并不是想像出去的,只是由两位在科罗拉多高校工作中的华籍专家教授――杨荣贵和尹晓波进行的创造发明,该科研成果早已在《科学》杂志期刊上发布。 这类材料是真实能够 大规模生产的便宜材料。从外部经济上看,这类新材料是由很多直徑在8μm上下的小夹层玻璃珠串任意地嵌入在全透明塑料中做成的。一般的塑料、一般的小玻璃弹珠,组成起來确是一种室内温度辐射源的“黑体字”。 这一黑体字塑料薄膜材料能够 以远红外线无线电波的方式向外辐射源动能进而做到降温的实际效果。并且,这类材料发送的电磁波波长是8~14μm。对这一光波长的动能,地球上的地球大气层基本上沒有一切摩擦阻力。换句话说,这种被发送的发热量几乎不被地球大气层根据反射、消化吸收和透射等方法“变换消化吸收”掉,只是立即越过地球大气层,进到外太空,一去不复返。品牌形象地说,这类“塑料”是大家定居的室内温度自然环境和外太空零下270℃的寒冷自然环境的动能运输安全通道,能够 源源不绝地把地球上运用不上的发热量运输出来。 假如在材料的反面再镀一层纳米其他陶瓷膜,降温实际效果会更好,不但能够 把发热量赶走,还能够反射自然光,阻拦必须降温的物件由于消化吸收太阳而变暖。试验显示信息,这类材料在中午太阳照射下最大达到93W/平米的辐射源制冷输出功率,能够 轻轻松松让与它触碰的物件降温10~16 ℃。 地球变暖一直是人们应对的一个一同课题研究。这类运用外太空零下270℃的蓄冷的新技术应用是处理地球变暖难题的一个新的探寻方位。专家教授们现阶段已经勤奋,争得将该材料早日商业化的,让大量人享有到它的益处,早日缓解地球变暖的发展趋势。 来源于:中国科学报 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |