| 牌号简介 About |
|---|
| Emerge PC 8130高级树脂是一种具有改进的紫外线稳定性的阻燃聚碳酸酯树脂。它是为薄壁应用而设计的，在1.0毫米处具有UL94V-0额定值。Emerge PC 8130也符合UL 746C的F1等级。该树脂不含氯或溴添加剂。主要特点：耐燃抗紫外线应用：动力装置外壳信息技术设备电气部件 EMERGE™ PC 8130 Advanced Resin is an ignition-resistant polycarbonate resin with improved UV stability. It is designed for thin-wall applications and has a UL94 V-0 rating at 1.0 mm. EMERGE PC 8130 is also f1 rated according to UL 746C. This resin does not contain chlorine or bromine additives. Main Characteristics: Ignition resistant UV resistant Applications: Powered Device Housings Information technology equipment Electrical parts |
产品描述 Product Description
用途：电器外壳;电气/电子应用领域;薄壁部件;外壳;
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-1; 无卤; 防火阻燃等级V-0; 防火阻燃等级5VB; 阻燃; 防火阻燃等级5VA; 易流动; 耐候抗UV; 5VA,Flame Characteristics,5VB,Good liquidity,V-0,Weather resistance is good,V-1,Halogen free
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density Density |
1.20 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
10 | g/10min | ASTM D1238 |
|
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
|
MD MD |
0.50 to 0.70 | % | ASTM D955 |
|
吸水率 Water Absorption Water Absorption |
|||
|
23℃，24hr 23℃，24hr |
0.15 | % | ASTM D570 |
|
耐候性 Weathering resistance |
f1 | UL 746C | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ASTM D638 | |
|
拉伸强度 Tensile Strength Tensile Strength |
|||
|
断裂 brk Broken BRK |
MPa | ISO 527-2/50 | |
|
断裂 brk Broken BRK |
MPa | ASTM D638 | |
|
屈服 yld Yield yld |
MPa | ISO 527-2/50 | |
|
屈服 yld Yield yld |
MPa | ASTM D638 | |
|
拉伸应变 Tensile Strain Tensile Strain |
|||
|
断裂 brk Broken BRK |
% | ASTM D638 | |
|
屈服 yld Yield yld |
% | ASTM D638 | |
|
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ASTM D790 | |
|
弯曲强度 Flexural Strength Flexural Strength |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
J | ASTM D3763 | |
|
拉伸冲击强度 Tensile Impact Strength Tensile Impact Strength |
kJ/m² | ASTM D1822 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT Hot deformation temperature HDT |
|||
|
1.8 MPa，未退火，6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ASTM D1525 | |
|
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
|
MD MD |
1/℃ | ASTM D696 | |
|
相对温度指数 Relative Temp Index(RTI) Relative Temperature Index (RTI) |
|||
|
电气性能 elec Electrical performance Elec |
℃ | UL 746 | |
|
强度机械性能 str Strength mechanical performance str |
℃ | UL 746 | |
|
冲击机械性能 imp Impact mechanical performance IMP |
℃ | UL 746 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
耐电弧性 Arc Resistance Arc Resistance |
ASTM D495 | ||
|
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
UL 746 | ||
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
0.9 mm 0.9 mm |
UL 746 | ||
|
1.0 to 3.0 mm 1.0 to 3.0 mm |
UL 746 | ||
|
高压电弧抗点燃指数（HVAR）（PLC） High voltage arc ignition resistance index (HVAR) (PLC) |
UL 746 | ||
|
热丝引燃（HWI）（0.9 to 3.0 mm） Hot wire ignition (HWI) (0.9 to 3.0 mm) |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame Class Rating Flame Class Rating |
Internal Method | ||
|
0.90 mm，所有颜色 0.90 mm, all colors |
Internal Method | ||
|
0.90 mm，黑色，白色 0.90 mm, black, white |
Internal Method | ||
|
1.00 mm，所有颜色 1.00 mm, all colors |
Internal Method | ||
|
2.00 mm，所有颜色 2.00 mm, all colors |
Internal Method | ||
|
3.00 mm，所有颜色 3.00 mm, all colors |
Internal Method | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
|
【新闻资讯】查看全部 
2017中国国际工程塑料创新与使用开展论坛
2017-09-22 2017中国国际工程塑料创新与应用发展论坛 2017China International Innovation and Application Development Forum of Engineeringplastics 时间 ：2017年10月25 -26 日 地点 ：重庆 一、 大会背景 工程塑料行业正急 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付