牌号简介 About |
---|
HD7000C是一种高密度聚乙烯,均聚物设计用于吹塑部分。HD7000C具有较高的刚度性能、良好的抗冲击性能、良好的表面质量和良好的感官性能。用途:吹塑小体积:润滑油、食用油、牛奶、果汁、酸奶瓶;玩具。流程:吹塑;IBM流程指示(注射吹塑)。 HD7000C is a high density polyethylene, homopolymer designed for the blow-molding segment. HD7000C shows high stiffness properties, good impact resistance, good surface quality and good organoleptic properties. Applications: Blow Molded Small Volume: Bottles for lubricant and edible oils, milk, juice and yogurt; Toys. Process: Blow Molding; Indication for IBM process (Injection Blow Molding). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.963 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.35 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
35 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
30.0 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
|||
1% 正割,模压成型 1% cut, molded |
1500 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
模压成型 Compression Molding |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,模压成型 0.45 MPa, unannealed, molded |
℃ | ASTM D648 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
中国石油无偿划转1%股份给中国石化
2022-09-08 扫描上图二维码,可以免费下载 搜料 APP 中国石油天然气股份有限公司日前发布公告称,公司于2022年9月5日收到公司控股股东中国石油集团有限公司(以下简称中国石油集团)发出的《 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |